Decoupling, Quantifying, and Restoring Aging-Induced Zn-anode Losses in Rechargeable Aqueous Zinc Batteries
Shengda D. Pu,Bingkun Hu,Zixuan Li,Yi Yuan,Chen Gong,Ziyang Ning,Chloe Chau,Sixie Yang,Shengming Zhang,Liquan Pi,Yuanbo T. Tang,Jili Yue,T. James Marrow,Xiangwen Gao,Peter G. Bruce,Alex W. Robertson
DOI: https://doi.org/10.1016/j.joule.2023.01.010
IF: 46.048
2023-01-01
Joule
Abstract:Rechargeable aqueous zinc batteries offer low cost, safety, and good cycling capacity, largely due to the water-compatible Zn-metal anode. However, Zn anodes corrode in aqueous electrolytes. While such corrosion is well known, distinguishing the relative importance of corrosion contributions toward anode capacity loss remains less understood. Here, by systematically cycling Zn anodes with controlled loading and under different aging conditions, we suc-cessfully decouple and quantify the aging-induced contributions to-ward anode degradation in mildly acidic aqueous electrolytes. While some losses occur due to the irreversible consumption of Zn into corrosion by-products, we demonstrate that the bigger contributor to this efficiency loss (over 80%) is the physical screening effect of evolved gases, preventing the reversible dissolution of deposited Zn. Understanding the crucial role of evolved gas during cell aging, and how it can accumulate and effectively passivate large sections of the battery anode, will have important implications in the develop-ment of rechargeable aqueous zinc batteries.