Abstract:In this paper, the substitution of different amounts of Zr for Ti in the hydrogen storage electrode alloy Mg35Ti10Ni55 has been carried out for the purpose of further improving the electrochemical performance of the electrode alloy. The electrochemical properties were tested on the purposely prepared Mg35Ti10−xZrxNi55 (x=1, 3, 5, 7, 9) electrode alloys. The results showed that all alloys substituted with Zr possessed a higher cycling capacity retention and a larger initial discharge capacity (except Mg35Ti1Zr9Ni55) than the original alloy Mg35Ti10Ni55. Among these alloys Mg35Ti5Zr5Ni55 exhibited the highest discharge capacity and cycling stability. It was found from X-ray Photoelectron Spectroscopy (XPS) surface analysis that the Zr content reduced the degree of oxidation of Mg. The higher the Zr content, the lower is the degree of oxidation of Mg. Auger electron spectroscopy (AES) analysis revealed that the thickness of the passive oxide film coating on the alloy surfaces became first reduced as the Zr content increased but subsequently became augmented as the Zr content exceeded 5 at.%. The study indicated that the corrosion inhibiting effect of Zr alone, without the presence of Ti was weak. The synergetic effect of Zr and Ti made the passive film more compact, less pervious and more protective than by Ti or Zr alone. The thickness of the passive film agreed well with the polarization resistance of the alloys obtained from electrochemical impedance spectroscopy (EIS) Nyquist diagrams, suggesting that the surface polarization resistance RP being closely related to the film thickness and the exchange current density on the surface of the alloy varied accordingly. The conclusion of this study is that 5 at.% Zr substitution in Mg35Ti10Ni55 leads to the formation on the surface of a good and thin passive film, which retards the corrosion of the alloy and at the same time leads to the least polarization resistance and highest exchange current in this series of alloys studied.

The influence of relative content of Ti and Zr on the electrochemical behavior of Laves phase alloy

Electrochemical Cycle Life of Zr-Based Laves Phase Alloys Influenced by Alloy Stoichiometry and Composition

The Effects of Partial Substitution of Mn by Cr on the Phase Structure, Microstructure and Electrochemical Properties of Ti-Zr-V-Mn-Ni Hydrogen Storage Alloys

The effect of partial substitution of Zr for Ti on the electrochemical properties and surface passivation film of Mg35Ti10 - xZrxNi55 (x=1, 3, 5, 7, 9) electrode alloys

Phase Structures and Electrochemical Properties of V2.1TiNi0.4Zrx (x=0−0.06) Hydrogen Storage Electrode Alloys

The effect of partial substitution of Ti with Zr, Cr or V in the Mg35Ti10Ni55 electrode alloy on its electrochemical performance

Improvement of electrochemical cyclic durability of Zr-based AB2 alloy electrodes

The Effects of Partial Substitution of Mn by Cr on the Electrochemical Cycle Life of Ti-Zr-V-Mn-Ni Alloy Electrodes of a Ni/MH Battery

Influence of Annealing Treatment on Microstructure and Cycling Stability of La-Rich Ml(Nicomnal)(5) Alloy Electrode for Ni/Mh Batteries

Electrochemical studies on the Ti–Zr–V–Mn–Cr–Ni hydrogen storage electrode alloys

The Effect of Zr Substitution for Ti on the Microstructures and Electrochemical Properties of Electrode Alloys Ti1−xZrxV1.6Mn0.32Cr0.48Ni0.6

The phase structure and electrochemical properties of the melt-spun alloy Zr0.7Ti0.3Mn0.4V0.4Ni1.2

The Effects of Titanium on the Phase Structure and Charge/Discharge Performance of Ml(Nicomnti)(5) Alloy

Effect of zr content on the microstructures and hydrogen storage properties of (Ti-Cr)(45-x)V55Zrx (x=1 similar to 7) alloys

Phase Structures and Electrochemical Properties of the Laves Phase Hydrogen Storage Alloys Zr1−xTix(Ni0.6Mn0.3V0.1Cr0.05)2

Corrosion and degradation behavior of Zr-based AB2 alloy electrodes during electrochemical cycling

Microstructure and Electrochemical Properties of V2.1TiNi0.4Zr0.06Cux (X=0-0.12) Hydrogen Storage Alloys

Effects of Some Factors on the Preparation of Zr-based AB2 Type Laves Phase Hydrogen Storage Alloy

Effect of rare earth composition on the electrochemical properties of multicomponent RENi5-xMx (M = Co, Mn, Ti) alloys

Microstructure and hydrogen storage properties of Ti10V84-xFe6Zrx (x = 1-8) alloys

Microstructure and Electrochemical Properties of V_(2.1)TiNi_(0.4)Zr_(0.06)Cu_(0.03)M_(0.10)(M=Cr, Co, Fe, Nb, Ta) Hydrogen Storage Alloys