Preparation, characterization and microwave absorption properties of NiFe2O4 and its composites with conductive polymer
Zhitao Li,Mingquan Ye,Aijun Han,Hui Du
DOI: https://doi.org/10.1007/s10854-015-3848-8
2015-10-19
Abstract:Spinel ferrite NiFe2O4 was synthesized by polyacrylamide sol–gel method, and its composites with polyaniline (PANI) and polypyrrole (PPY) were prepared via in situ emulsion polymerization. The morphology of NiFe2O4 had a flake structure, while that of NiFe2O4/PANI and NiFe2O4/PPY composites existed a flake-grain structure. The magnetic properties (Ms, Mr and Hc) of NiFe2O4/PPY were lower than those of NiFe2O4/PANI, and they were all lower than those of NiFe2O4. NiFe2O4/PPY composite exhibited a higher conductivity value of 3.76 S/cm than that of NiFe2O4 and NiFe2O4/PANI. Moreover, the imaginary part of permittivity also enhanced with the increase of conductivity, contributing to the increase of dielectric loss. The electromagnetic characteristics of NiFe2O4, NiFe2O4/PANI and NiFe2O4/PPY were also investigated with a vector network analyzer in 1–18 GHz. The absorbing peak position moved to lower frequency with the increasing thickness of NiFe2O4/PANI or NiFe2O4/PPY composites. Under the same condition, the minimum reflection loss of NiFe2O4/PPY was much lower than that of NiFe2O4 and NiFe2O4/PANI, indicating the incorporation between NiFe2O4 and PPY could reach a better matching in terms of electromagnetic parameters. The value of the minimum reflection loss was −42 dB at 8 GHz for NiFe2O4/PPY with a thickness of 3.5 mm, and a broad peak with a bandwidth lower than −10 dB was about 4.5 GHz.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied