Abstract:A high soluble and stable epsilon-Zn(OH)(2) precursor is synthesized at below room temperature to efficiently prepare ZnO whiskers. The experimental results indicate that the formation of ZnO whiskers is carried out mainly via two steps: the formation of ZnO seeds from epsilon-Zn(OH)(2) via the in situ solid conversion, and the following growth of whiskers via dissolution-precipitation route. The decrease of temperature from 25 to 5 degree celsius promotes the formation of epsilon-Zn(OH)(2) with higher solubility and stability, which balances the conversion and dissolution rates of precursor. The Rietveld refinement, DFT calculations and MD simulations reveal that the primary reason for these characteristics is the expansion of e-Zn(OH)(2) lattice due to temperature, causing difficulties in the dehydration of adjacent OH. Simultaneously, the larger specific surface area favors the dissolution of epsilon-Zn(OH)(2). Based on this precursor, well-dispersed ZnO whiskers with 9.82 mu m in length, 242.38 nm in diameter, and an average aspect ratio of 41 are successfully synthesized through a SDSN-assisted hydrothermal process at 80 degree celsius. The process has an extremely high solid content of 2.5% (mass ratio of ZnO to solution) and an overall yield of 92%, which offers a new approach for the scaled synthesis of high aspect ratio ZnO whiskers by liquid-phase method.

Sol–gel Process of ZnO and ZnAl 2 O 4 Coated Aluminum Borate Whiskers

Study on Preparation of MgO Crystal Whisker from Magnesite

Preparation of ZrO 2 whiskers through high pressure and high temperature method

Preparation of Chromium Oxide Coatings on Aluminum Borate Whiskers by a Hydrothermal Deposition Process

Effects of Zno Coating of Whiskers on the Tensile Properties and Aging Behaviors of Aluminum Borate Whiskers Reinforced 2024al Composite

THERMAL DECOMPOSITION AND CRYSTALLIZATION PROCESS OF ZnO:Al THIN FILMS VIA SOL-GEL ROUTE

Formation mechanism of whiskers in Al–MgAl2O4–MgO refractories at 1400 °C under N2 atmosphere

Preparation of Zirconia Powders by Sol-gel Process

Preparation and Characterization of Monoclinic Rod-Shaped ZrO 2 Whiskers Via Sulfate Flux

Tensile Properties and Thermal Stability of ZnO-coated Aluminum Borate Whiskers Reinforced 2024al Composite

Sol–gel alumina coatings for whisker reinforced metal matrix composites

Mechanical Properties and Thermal Stability of Znal2o4-Coated Aluminum Borate Whiskers Reinforced 2024al Composite

Effects of Cr 2O 3 coating of whiskers on the tensile properties and thermal stability of aluminum borate whiskers reinforced 2024Al composite

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

INTERFACE MODIFICATION OF THE ALUMINUM BORATE WHISKER REINFORCED 6061Al COMPOSITE

Surface Synthesis of Aluminum Borate Whiskers on the ZTA Ceramics and Its Application to Joining

Fine structure of coated whiskers in Al18B4O33w/γ-Al2O3/6061Al composite

Effects of ZnO Coating on the Wettability and Tensile Properties of Aluminum Borate Whisker-Reinforced Aluminum Composite

Synthesis and Mechanism of 1D ZnO Based on Alkaline Dissolution‐Conversion Strategy of High Stable and Soluble Ɛ‐zn(oh)2

Synthesis and microstructural characterization of aluminum borate whiskers

Study on preparing technology of MgO whisker with MgSO_4 as raw material