Abstract:To improve the wear resistance of TC4 titanium alloy, two types of wear-resistant coatings were applied to the surface using laser melting: Ni60 + 50% WC and d22 powder priming. The phase composition and microstructure of the coatings were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM), and energy spectroscopy (EDS). The mechanical properties of the coating were tested using an HV-1000 micro-Vickers hardness tester, an HRS-2M high-speed reciprocating friction and wear tester, and a WDW-100D electronic universal testing machine. The results show that Ni60 + 50% WC composite coating and d22 priming + (Ni60 + 50% WC) composite coating mainly consist of W2C, TiC, Ni17W3, Ni3Ti, and TixW1−x phases. Compared to the TC4 substrate, the microhardness of both coatings is significantly higher, approximately 2.8 times the microhardness of the substrate. In frictional wear experiments, the average friction factors of the two coatings and the TC4 substrate are 0.476, 0.55, and 0.865, respectively, and the wear of the two coatings is only 0.0559–0.0769 that of the TC4 substrate, with a significant increase in wear resistance, nearly 17 times higher than that of the substrate. The coating shows flaking, shallow abrasion marks, and granular debris, dominated by adhesive wear and fatigue wear, while the TC4 substrate shows more furrows on the surface, dominated by abrasive wear. The shear bond strengths of the Ni60 + 50% WC composite coating and the d22 powder primed + (Ni60 + 50% WC) composite coating were 188.19 MPa and 49.11 MPa, respectively. Conclusion: both coatings significantly improve the hardness and wear resistance of the TC4 titanium alloy substrate surface, with the Ni60 + 50% WC composite coating performing better in hardness, wear resistance, and bond strength.

Research of Laser Remelting Nickel-Coated Graphite Layer on Titanium Alloy Substrate

Ni–TiC Coating Deposited on Ti–6Al–4V Substrate by Thermal Spraying and Laser Remelting of Ni-clad Graphite Powder

Laser Cladding Nicocraly Coating on Ti-6al4v

Study on Interface Microstructure and Laser Re-melting NiCrBSi+TiN Coating

Microstructure and Wear Resistance of a Composite Coating Prepared by Laser Alloying with Ni-Coated Graphite on Ti-6Al-4V Alloy

Study on Microstructure of Laser Remelted NiCrBSi+TiN Coatings on Surface of Tianium Alloy

Laser Cladding Ni-Base Composite Coating on Titanium Alloy with Pre-Placed B4C+NiCoCrAlY

Influence of Scanning Speed on the Microstructure and Wear Resistance of Laser Alloying Coatings on Ti-6Al-4V Substrate

Wear Resistance of Thermal Spraying Nickel-Coated Graphite Layer on Titanium Alloy

Study of the Performance of Laser Melting Wear-Resistant Coatings on TC4 Titanium Alloy Surfaces

Microstructure and Wear Resistance of Ti6Al4V Titanium Alloy Laser-Clad Ni60/WC Composite Coating

Research on In-Situ Formation of Tic Particles Reinforced Nickel Base Alloy Coating Produced by Laser Cladding

In-Situ Synthesis of Metal Matrix Composite Coating with Laser Melting-Solidifying Processes

Microstructure Evaluation and High-Temperature Wear Performance of Hard Protective Layer Deposited on Titanium Alloy via Laser Metal Deposition

Microstructure and Properties of Al_2O_3-13wt%TiO_2 Coatings Fabricated by Plasma Spraying and Laser Remelting on Titanium Alloy

Laser Surface Remelting of Plasma Sprayed Nanostructured Al2O3–13wt%TiO2 Coatings on Titanium Alloy

Microstructure and Mechanical Properties of Ti-6Al-4V Prepared by Nickel Preplating and Electron Beam Surface Remelting

Microstructure and performance optimization of laser cladding nano-TiC modified nickel-based alloy coatings

Enhancing Hardness and Wear Performance of Laser Additive Manufactured Ti6Al4V Alloy Through Achieving Ultrafine Microstructure

Laser Surface Alloying of Pure Titanium with TiN–B–Si–Ni Mixed Powders

Research on Microstructure Properties of the TiC/Ni-Fe-Al Coating Prepared by Laser Cladding Technology