Microstructure and Enhanced Magnetic Properties of Low-Temperature Sintered LiZnTiMn Ferrite Ceramics with Bi2O3-Al2O3 Additive
Yulong Liao,Yaoying Wang,Zhenwei Chen,Xiaoyi Wang,Jie Li,Rongdi Guo,Cheng Liu,Gongwen Gan,Gang Wang,Yuanxun Li,Huaiwu Zhang
DOI: https://doi.org/10.1016/j.ceramint.2019.08.286
IF: 5.532
2020-01-01
Ceramics International
Abstract:Bi2O3 and Al2O3 were proven to separately have an impact on grain growth of LiZn ferrite ceramics. In this study, we synthesized LiZnTiMn ferrite ceramics under low temperature ( < 920 degrees C) using rationally designed formula of Bi2O3-Al2O3 as sintering agents. Microstructures, densities, and ferromagnetic performances were systematically investigated. Results show that appropriate amount of Bi2O3-Al2O3 leads to successful sintering of LiZnTiMn ferrites even below 900 degrees C. X-Ray diffraction (XRD) and scanning electron microscopy (SEM) results show that spinel structure ferrite ceramics were obtained and that the addition of Bi2O3-Al2O3 accelerated solidstate reaction. Corresponding ferromagnetic properties, including saturation induction (B-s), remanence square ratio, coercivity (H-c), ferromagnetic resonance linewidth (Delta H), and M-s, were also investigated. At 920 degrees C, with addition amount of x=1 Wt%, we obtain excellent performance: B-s=306 mT, B-r/B-s=0.849, H-c=2.34Oe, and Delta H=275 Oe. Results indicate that Bi2O3-Al2O3 is promising sintering agent for low-temperature sintering of LiZnTiMn ferrite ceramics.