Abstract:We report the synthesis of faceted single crystalline ZnO nanonecklace (ZnO NN) arrays horizontally aligned on r-plane sapphire using Au nanoparticles catalyzed chemical vapor deposition. High resolution TEM data show that ZnO NNs, without any grain boundary observed, grow along the ZnO [0001] direction horizontally oil r-plane sapphire and also reveal the epitaxial relationships between the ZnO NN and r-plane sapphire with ZnO [0001] parallel to sapphire [10 (1) over bar1] and ZnCl ((1) over bar2 (1) over bar0) parallel to sapphire (01 (1) over bar2). It was found that the Au nanoparticles with diameter of similar to 5 nm and lower particle density are critical for the formation of horizontally aligned ZnO NN arrays, while the larger size or the higher density of Au nanoparticles results in other types of ZnO nanostructures, Such as vertical ZnCl nanoblades and nanowires. Thermodynamic analysis indicates that faster increase of strain energy compared to slower increase of surface free energy and interfacial energy with size increase of one-dimensional ZnO nanostructures might be the critical reason for the size effect that controls the vertical vs horizontal growth of ZnO nanostructures. The smaller lattice mismatch of 1.5% in the growth direction (ZnO [0001] parallel to sapphire [10 (1) over bar1]) compared to the larger lattice mismatch of 18.3% in the other horizontal direction (ZnO [10 (1) over bar0] parallel to sapphire [2 (1) over bar(1) over bar0]) that is normal to the growth direction contributes to the one-dimensional growth. The width of ZnO NNs increases with growth time, indicative of continuous postgrowth deposition of ZnO on ZnO NNs. The evolution of necklacelike structures Of ZnO might be related to liquid catalyst surface tension, lattice mismatch/strain energy, and Surface decoration of ZnO facets with Al and Au atoms.

Crystallographic Alignment of ZnO Nanorod Arrays on Zn2GeO4 Nanocrystals: Promising Lattice-Matched Substrates

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Vapor phase growth and photoluminescence of oriented-attachment Zn2GeO4 nanorods array

Heteroepitaxial Growth of ZnO Nanorod Arrays on GaAs (111) Substrates by Electrochemical Deposition

On the formation of well-aligned ZnO nanowall networks by catalyst-free thermal evaporation method

Al2O3 buffer-facilitated epitaxial growth of high-quality ZnO/ZnS core/shell nanorod arrays

Low-temperature Growth and Raman Scattering Study of Vertically Aligned ZnO Nanowires on Si Substrate

Epitaxial Growth Of Horizontally Aligned Zinc Oxide Nanonecklace Arrays On R-Plane Sapphire

Controllable Growth of Highly Ordered ZnO Nanorod Arrays Via Inverted Self-Assembled Monolayer Template.

Synthesis and Optical Properties of Well-Aligned ZnO Nanorod Array on an Undoped ZnO Film

Aligned ZnO Nanorod Arrays Fabricated on Si Substrate by Solution Deposition

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Chemical Vapor Deposition-Based Growth of Aligned ZnO Nanowires on Polycrystalline Zn2GeO4:Mn Substrates

Oriented growth of ZnO nanostructures on Si and Al substrates

Controlled Growth of Well-Aligned Zno Mirco/Nanorod Arrays on Gan Substrates Using A Novel Solution Method

Well-Aligned Zno Nanocolumns Grown by Reactive Electron Beam Evaporation

Wet Chemical Approaches to Patterned Arrays of Well-Aligned ZnO Nanopillars Assisted by Monolayer Colloidal Crystals

Optoelectronic Properties Of Single-Crystalline Zn2geo4 Nanowires

Aligned ZnO Nanorods with Tunable Size and Field Emission on Native Si Substrate Achieved Via Simple Electrodeposition

Crystallographic Alignment of High Density Gallium Nitride Nanowire Arrays

Low-temperature Heteroepitaxy of Morphology-controlled ZnO Mirco/Nanorod Arrays on GaN Substrates