Abstract:Co-Cu exhibits a metastable miscibility gap in the region of the undercooled melt. Specimens have been undercooled and solidified containerlessly into the metastable miscibility gap in an electromagnetic levitation facility (EML) and in drop tube (DT) experiments. Due to the high undercooling the velocity of the solidification front is very high and the microstructure is frozen in instantaneously. The microstructure of samples processed in the EML is influenced by the electromagnetic stirring due to the induction of electrical currents into the melt. A variety of microstructures has been observed. After undercooling below the binodal the liquid melt separates into the Co-rich L1-phase and the Cu-rich L2-phase. Two basic morphologies of the L1-phase can be observed, they can be attributed to the transition in dendrite growth from diffusionally and thermally controlled to only thermally controlled growth. Transient microstructures are observed after solidification in the vicinity of the binodal. Drop tube experiments, which lead to a rapid solidification of a distribution of droplets under reduced gravity conditions, in contrary allow for the observation of the early stages of demixing: the microstructure shows a homogeneous distribution of spherical particles of the n-ltinority phase in the droplets. The cooling rate of the droplets and its dependence on the droplet radius has been calculated. The solidification velocity as a function of undercooling has been measured in the EML for the composition Co-18.8at%Cu. The data are analysed in the framework of the LKT/BCT model with a velocity-dependent distribution coefficient as well as within a model of Galenko and Danilov using a kinetic growth coefficient of mu=0.22 m/Ks.

Peritectic Solidification of Highly Undercooled Cu-Co Alloy

Containerless Rapid Solidification of Undercooled Cu-Co Peritectic Alloys

Peritectic Solidification under High Undercooling Conditions

Containerless Solidification Processing and Phase-Field Simulation for Ternary Fe-Cu-Co Peritectic Alloy under Reduced-Gravity Conditions

Solidification behaviour of undercooled Co–Cu alloys showing a metastable miscibility gap

Metastable Phase Separation and Rapid Solidification of Undercooled Co-Cu Alloy under Different Conditions

Dynamics of Solidification and Microstructure Evolution in Undercooled Co-Cu-Alloys with Metastable Miscibility Gap

RAPID SOLIDIFICATION OF UNDERCOOLED Co_(85)Cu_(15) HYPOPERITECTIC ALLOY

Electrical property of rapidly solidified Co-Cu peritectic alloys

Solidification Pathways of Ternary Cu 62.5 Fe 27.5 Sn 10 Alloy Modulated Through Liquid Undercooling and Containerless Processing

Phase separation and rapid solidification of liquid Cu 60 Fe 30 Co 10 ternary peritectic alloy

Phase separation and rapid solidification of liquid Cu<sub>60</sub>Fe<sub>30</sub>Co<sub>10</sub> ternary peritectic alloy

Rapid solidification of Cu84Co16 alloy undercooled into the metastable miscibility gap under different conditions

Rapid Solidification of Undercooled Cu–Ge Peritectic Alloy

Effect of Minor Addition of Co on Nonequilibrium Solidification of Deeply Undercooled Cu Based Alloys

Phase Selection and Microstructure Evolution of Undercooled Fe-Cu Peritectic Alloy

Metastable Phase Separation and Rapid Solidification of Undercooled Co 40 Fe 40 Cu 20 Alloy

Core-shell Microstructure Formed in the Ternary Fe-Co-Cu Peritectic Alloy Droplet

Rapid solidification mechanism of highly undercooled ternary Cu 40 Sn 45 Sb 15 alloy

Metastable Phase Separation And Rapid Solidification Of Undercooled Co40fe40cu20 Alloy

Microstructure analysis of Co–Cu alloys undercooled prior to solidification