Abstract:Statement of problem: New production methods have been developed for metal-ceramic restorations. Different production methods may show different surface roughness and fit, which may affect retention and long-term success. Purpose: The purpose of this in vitro study was to examine 3 different production methods with regard to surface roughness, marginal and internal fit, and retention of cobalt-chromium alloy single-crown copings. Material and methods: A master abutment of a premolar mandibular tooth preparation with 4-mm height and a 0.6-mm deep 120-degree chamfer finish line with a 12-degree angle of convergence was replicated in die stone and scanned. Thirty-six cobalt-chromium alloy copings were produced using 3 different production techniques. Twelve copings were produced by laser-sintering, 12 by milling, and 12 by milled wax/lost wax. The surface microstructure of 2 copings in each group was analyzed using interferometry. The remaining 10 copings in each group were used to evaluate marginal and internal fit by using an impression material replica method, and retention was evaluated by using a uniaxial tensile force pull-off test. The copings from each test group were cemented with zinc phosphate cement onto resin abutments. Statistical analyses of differences in marginal and internal fit were performed using 1-way ANOVA and the Mann-Whitney U test. Differences in surface topography were analyzed with the Kruskal-Wallis and Mann-Whitney U tests for nonparametric data. Differences in retentive values were analyzed using the Mann-Whitney U test for nonparametric data (all α=.05). Results: Differences in surface microstructure were seen. The laser-sintered copings showed increased surface roughness compared with milled and milled wax/lost wax copings. Differences in marginal and internal fit were noted. Laser-sintered showed significantly smaller spaces between coping and abutment than milled wax/lost wax copings (P=.003). At the margins, laser-sintered copings showed significantly smaller spaces than either the milled wax/lost wax group (P=.002) or the milled group (P=.002). At the chamfer, laser-sintered copings showed significantly smaller spaces than milled wax/lost wax copings (P=.005). At the center of the axial walls, laser-sintered copings showed significantly smaller spaces than those in the milled wax/lost wax (P=.004) and milled copings (P=.005). No significant differences were noted between milled and milled wax/lost wax copings (P>.05). No significant differences were detected regarding retentive forces in the pull-off tests (P>.05). Conclusions: Laser-sintered Co-Cr crown copings showed increased surface roughness and better internal and marginal fit than copings produced by milling or milled wax/lost wax technique. However, the crown pull-off tests did not reveal any significant differences.

A vitro study of marginal adaptation of different fabrication methods on copings

Effect of Machining Method and Margin Design on the Accuracy and Margin Quality of Monolithic Zirconia Crowns

[Comparative Adaptation of Crowns of Selective Laser Melting and Wax-Lost-casting Method].

Three-Dimensional Analysis of Internal Adaptations of Crowns Cast from Resin Patterns Fabricated Using Computer-Aided Design/Computer- Assisted Manufacturing Technologies

Evaluation on the Marginal Adaptation of CAD/CAM Ceramic Crown

Marginal adaptation of crown by national CAD/CAM

Marginal discrepancy of 3-unit Co-Cr metal copings fabricated with additive and subtractive manners: A comparative study

Effect of porcelain firing and cementation on the marginal fit of implant-supported metal-ceramic restorations fabricated by additive or subtractive manufacturing methods

In Vitro Marginal Adaptation of Single Crowns Fabricated from Several Provisional Resins

Effect of production method on surface roughness, marginal and internal fit, and retention of cobalt-chromium single crowns

Clinical Marginal and Internal Fit of Crowns Fabricated Using Different CAD/CAM Technologies

Comparation of marginal and internal adaption of endocrowns made from three different ceramics in vitro

Influence of impression method and shoulder design on the marginal adaptation of CAD/CAM nanoceramic resin onlay restorations

Marginal fit of 3-unit implant-supported fixed partial dentures: Influence of pattern fabrication method and repeated porcelain firings

Study of 3DP Technique in Wax Pattern of Dental Inner Coping

Evaluation of the fit of Ti2448 and titanium copings fabricated by Wieland CAD/CAM system

Dimensional accuracy and internal and marginal fit evaluation of Co-Cr crowns prepared by SLM

CAD‐CAM and heat‐press: Comparison of internal and marginal fit of lithium disilicate copings

Effects of fabrication techniques on denture base adaptation: An in vitro study

Effect of Tooth Preparation Design on Marginal Adaptation of Composite Resin CAD-CAM Onlays

AN IN VITRO COMPARISON OF OVERALL FIT OF COBALT-CHROMIUM COPINGS CASTED CONVENTIONALLY FROM INLAY CASTING WAX, PATTERN RESIN & 3D PRINTED RESIN EVALUATED BEFORE & AFTER CERAMIC FIRING CYCLES