Origin of the Ultrafast Response of the Lateral Photovoltaic Effect in Amorphous MoS2/Si Junctions.
Chang Hu,Xianjie Wang,Peng Miao,Lingli Zhang,Bingqian Song,Weilong Liu,Zhe Lv,Yu Zhang,Yu Sui,Jinke Tang,Yanqiang Yang,Bo Song,Ping Xu
DOI: https://doi.org/10.1021/acsami.7b04298
IF: 9.5
2017-01-01
ACS Applied Materials & Interfaces
Abstract:The lateral photovoltaic (LPV) effect has attracted much attention for a long time because of its application in position-sensitive detectors (PSD). Here, we report the ultrafast response of the LPV in amorphous MoS2/Si (a-MoS2/Si) junctions prepared by the pulsed laser deposition (PLD) technique. Different orientations of the built-in field and the breakover voltages are observed for a-MoS2 films deposited on p- and n-type Si wafers, resulting in the induction of positive and negative voltages in the a-MoS2/n-Si and a-MoS2/p-Si junctions upon laser illumination, respectively. The dependence of the LPV on the position of the illumination shows very high sensitivity (183 mV mm-1) and good linearity. The optical relaxation time of LPV with a positive voltage was about 5.8 μs in a-MoS2/n-Si junction, whereas the optical relaxation time of LPV with a negative voltage was about 2.1 μs in a-MoS2/p-Si junction. Our results clearly suggested that the inversion layer at the a-MoS2/Si interface made a good contribution to the ultrafast response of the LPV in a-MoS2/Si junctions. The large positional sensitivity and ultrafast relaxation of LPV may promise the a-MoS2/Si junction's applications in fast position-sensitive detectors.