Abstract:Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications, Ahead of Print. The work reports on synthesis and comprehensive evaluation of different properties of a bilayer protective coating on Mg alloy of AZ91D grade. Initially the alloy substrates were treated in stannate bath for 15, 30, 45, 60, 75 and 90 min for synthesizing an MgSnO3.3H2O layer. Electroless Ni-P was then deposited for 30 and 60 min, on the stannate layer synthesized for 60 min. A time-dependent cyclic growth behaviour was observed for stannate layers, characterized by formation and dissolution of MgSnO3.3H2O globules. The stannate coatings displayed polycrystalline structure. Hardness and scratch resistance were strongly influenced by uniformity of the coatings. While the uncoated alloy exhibited hardness of only 93 HV0.05, a remarkable improvement in hardness to 484 HV0.05 was obtained after 60 min of stannate treatment. High critical load of adhesion (Lc3) of 29 N was also obtained for the same. The stannate layers exhibited coefficient of friction (CoF) of 0.4–0.6 as compared to 0.7–0.8 for bare alloy. The wear loss also notably reduced. In tribo-test, hard and well-adherent coating restricted surface deformation under action of normal load. This in-turn, reduced mechanical engaging at interface, leading to low CoF and wear loss. The dense stannate coating also reduced corrosion rate by 19 times by hindering penetration of corrosive medium. Electroless deposition for 30 min on stannate conversion layer yielded only sporadic growth of Ni-P, which improved to a dense, uniform layer after 60 min of deposition. The Ni-P top coating aided the stannate underlayer in furthering the tribo-mechanical and corrosion characteristics.

In-Situ Study of the Formation Process of Stannate Conversion Coatings on Az91d Magnesium Alloy Using Electrochemical Noise

Electrochemical Noise Characteristics in Corrosion Process of Az91d Magnesium Alloy in Neutral Chloride Solution

ELECTROCHEMICAL NOISE OF AZ31 MAGNESIUM ALLOY IN NaCI SOLUTION

In-situ monitoring of pitting corrosion of AZ31 magnesium alloy by combining electrochemical noise and acoustic emission techniques

Study of the Zinc Electroplating Process Using Electrochemical Noise Technique

In-situ Monitoring of Nickel Electrodeposit Structure Using Electrochemical Noise Technique

Electrochemical noises of LC4, LY12 and pure Al in NaCl solution

In-situ monitoring of pitting corrosion of Q235 carbon steel by electrochemical noise: Wavelet and recurrence quantification analysis

Study on the Anodic Film Formation Process of AZ91D Magnesium Alloy

A Preliminary Study of the Relationship Between Zinc Deposit Morphology and Electrocrystallization Noise

Analysis of Pitting Corrosion Behavior of Pure Al in Sodium Chloride Solution with the Wavelet Technique

Electrochemical noise features of pure aluminum during pitting corrosion in neutral NaCl solution

Composite Electroless Nickel-nano Al2O3 Coatings on Steel Substrate

Electrochemical noise comparative study of pitting corrosion of 316L stainless steel fabricated by selective laser melting and wrought

Electrolytic Deposition of Hydroxyapatite Coating on CoNiCrMo Substrates

PREPARATION AND CORROSION ELECTROCHEMISTRY BEHAVIOR OF CERIUM-BASED CHEMICAL CONVERSION COATING ON AZ91 MAGNESIUM ALLOY

Electrochemical Noise Analysis Using Experimental Chaos Theory, Power Spectral Density and Hilbert–Huang Transform in Anodized Aluminum Alloys in Tartaric–Phosphoric–Sulfuric Acid Solutions

In-situ visualization of corrosion behavior of Al CoCrFeNi high-entropy alloys during electrochemical polarization

Synthesis and evaluation of tribo-mechanical and corrosion properties of electroless Ni-P coating on AZ91D Mg alloy with stannate conversion underlayer

Nano Al2O3/phosphate composite conversion coating formed on magnesium alloy for enhancing corrosion resistance

Potentiostatic Electrochemical Noise Analysis of 2101 Lean Duplex Stainless Steel in 1 mol/L NaCl