Abstract:In this paper, a Ni coating was deposited on the surface of the A356 aluminum alloy by high velocity oxygen fuel spraying to improve the performance of the AZ91D magnesium/A356 aluminum bimetal prepared by a compound casting. The effects of the Ni coating as well as its thickness on microstructure and mechanical properties of the AZ91D/A356 bimetal were systematically researched for the first time. Results demonstrated that the Ni coating and its thickness had a significant effect on the interfacial phase compositions and mechanical properties of the AZ91D/A356 bimetal. The 10µm's Ni coating cannot prevent the generation of the Al-Mg intermetallic compounds (IMCs) at the interface zone of the AZ91D/A356 bimetal, while the Ni coating with the thickness of 45 µm and 190 µm can avoid the formation of the Al-Mg IMCs. When the Ni coating was 45 µm, the Ni coating disappeared and transformed into Mg-Mg2Ni eutectic structures+Ni2Mg3Al particles at the interface zone. With a thickness of 190µm's Ni coating, part of the Ni coating remained and the interface layer was composed of the Mg-Mg2Ni eutectic structures+ Ni2Mg3Al particles, Mg2Ni layer, Ni solid solution (SS) layer, Al3Ni2 layer, Al3Ni layer and sporadic Al3Ni+Al-Al3Ni eutectic structures from AZ91D side to A356 side in sequence. The interface layer consisting of the Mg-Ni and Al-Ni IMCs obtained with the Ni coating had an obvious lower hardness than the Al-Mg IMCs. The shear strength of the AZ91D/A356 bimetal with a Ni coating of 45 µm thickness enhanced 41.4% in comparison with that of the bimetal without Ni coating, and the fracture of the bimetal with 45µm's Ni coating occurred between the Mg matrix and the interface layer with a mixture of brittle fracture and ductile fracture.

Synthesis and evaluation of tribo-mechanical and corrosion properties of electroless Ni-P coating on AZ91D Mg alloy with stannate conversion underlayer

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Multilayer Ni-P Coating for Improving the Corrosion Resistance of Az91d Magnesium Alloy

Microstructure, Friction and Wear Behavior and Corrosion Resistance of electroless Double-Layer Ni-P/Ni-Mo-P Coatings on AZ91D Magnesium Alloy

Electroless Ni–P deposition plus zinc phosphate coating on AZ91D magnesium alloy

Corrosion resistance of AZ91D magnesium alloy with electroless plating pretreatment and Ni–TiO2 composite coating

High Corrosion-Resistance Nanocrystalline Ni Coating on AZ91D Magnesium Alloy

Preparation and properties of nano ZrO2 coating on magnesium alloy

Electrodeposition of High Corrosion Resistance Cu/Ni–P Coating on AZ91D Magnesium Alloy

Microstructures and corrosion resistance of conversion film-electroless Ni-W-P ternary coatings on AZ91D magnesium alloy

Stearic acid modified porous nickel-based coating on magnesium alloy AZ31 for high superhydrophobicity and corrosion resistance

A study on properties of electroless Ni-B/MgB2 coatings on AZ91 magnesium alloy

Superior corrosion and wear resistance of AZ91D Mg alloy via electrodeposited SiO2–Ni-based composite coating

Effect of Mg on Al-Mg Alloy and Electroless Ni-P Codeposition of nano-Al2O3: Mechanical, Wear, and Corrosion Resistance Properties

A nickel-underlayer/LDH-midlayer/siloxane-toplayer composite coating for inhibiting galvanic corrosion between Ni layer and Mg alloy

Improving mechanical properties of AZ91D magnesium/A356 aluminum bimetal prepared by compound casting via a high velocity oxygen fuel sprayed Ni coating

Wear and Corrosion Properties of 316L-SiC Composite Coating Deposited by Cold Spray on Magnesium Alloy

Microstructure and Electrochemistry Behavior of Ni-Cu-P Ternary Nickel-Based Amorphous Coating

Analysis of the Causes of Differences between the Upper and Lower Surfaces of Electroless Ni–P Coating on LZ91 Magnesium–Lithium Alloy

Mechanical Properties of Al2o3/Al Bi-Layer Coated Az91 Magnesium Alloy

Electrodeposition and corrosion resistance of Ni–P–TiN composite coating on AZ91D magnesium alloy