Abstract:In order to study the mechanical properties of seawater sea sand concrete and the durability damage law of seawater sea sand concrete under the action of seawater erosion, corresponding specimens were prepared and subjected to cube compressive strength, flexural strength, and dry-wet cycle tests by taking the volume dosage of glass fibers and polyvinyl alcohol fibers as variables. The test combined SEM scanning and EDS to analyze the microstructure of fiber-reinforced seawater sand concrete, and established a model based on the two-parameter Weibull probability distribution. The results show that the fiber has a significant effect on improving the mechanical properties and erosion resistance of seawater sand concrete. When the total volume content is 0.3% and the mixing ratio is 1:1, the improvement effect is the best. The maximum increase in cubic compressive strength was 24.2%; the maximum increase in flexural strength was 38.8%. After the specimens were subjected to wet and dry cycles for 360d, the maximum reduction in mass loss rate was 41.23%; the maximum reduction in strength loss rate was 27.55%. As observed from the microscopic images, the main disadvantage of SSC is that the salt crystallization and swelling matter produced by the erosion ions will weaken the bond between aggregate and mortar, resulting in defects in the interfacial transition zone (ITZ). Under the action of dry-wet cycles, the alternating dry-wet forces, the expansion pressure generated by expansive substances and the crystallization pressure generated by salt crystallization will change the microstructure, and therefore the damage of the specimen will deepen with the extension of erosion time. The microscopic images also show that the doping fibers can improve the internal integrity and compactness of the matrix, thus significantly improving the mechanical properties and durability of seawater sea sand concrete. In this test, a damage model was established based on the two-parameter Weibull distribution model, and the damage law between strength loss and dry-wet cycles was fitted, which provides a favorable basis to study the damage of seawater sea sand concrete under wet-dry cycling.

Study the Corrosion of Drying-Wetting Sulfates on Washed Sea Sand Concrete

Study on the Deterioration of Concrete under Dry-Wet Cycle and Sulfate Attack

Study on Concrete Deterioration and Chloride Ion Diffusion Mechanism by Different Aqueous NaCl-MgSO4 Concentrations

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Damage Mechanism of Concrete Deteriorated by Sulfate Attack in Wet-Dry Cycle Environment

Study on Corrosion Mechanism of Different Concentrations of Na2SO4 Solution on Early-Age Cast-In-Situ Concrete

Study on Concrete Deterioration in Different NaCl-Na2SO4 Solutions and the Mechanism of Cl- Diffusion

Degradation Mechanisms of Chloride Contaminated Cast-in-Situ Concrete Partially Exposed to Magnesium-Sulfate Combined Environment

Experimental study of the deterioration mechanism of concrete under sulfate attack in wet-dry cycles

Effects of Sodium Sulfate Attack on Concrete Incorporated with Drying-Wetting Cycles

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack

Effect of Dry–Wet Ratio on Properties of Concrete Under Sulfate Attack

Study on the deterioration of concrete performance in saline soil area under the combined effect of high low temperatures, chloride and sulfate salts

Study on mechanical properties and anti-erosion performance of fiber reinforced seawater sea sand concrete

Combined effects of sulfate attack under drying–wetting cycles and loading on the fatigue behavior of concrete

Degradation effect of seawater on the long-term dynamic behavior of artificially cemented sand

Degradation progress of Portland cement mortar under the coupled effects of multiple corrosive ions and drying-wetting cycles

Mechanical Properties and Damage Evolution of Concrete Materials Considering Sulfate Attack

Damage Constitutive Model and Mechanical Performance Deterioration of Concrete under Sulfate Environment

Influence of Chemical Corrosion on Pore Structure and Mechanical Properties of Sandstone