Abstract:Using cobaloxime boron fluoride (COBF) and AIBN as catalyst and initiator respectively, the catalytic chain transfer bulk polymerization of 2-hydroxyporpyl methacrylate ( HPMA) was carried out at 60 degrees C and the low molecular weight polymer with a terminal double bond was prepared. The evolution of the apparent chain transfer constant (C-S(spp)) of COBF during the polymerization was determined by the Mayo equation and the CLD (chain length distribution) equation respectively. At the beginning of the reaction the chain transfer constant showed values of up to about 2000, but with the increasing of the monomer conversion, the chain transfer constant decreases and keeps at a value of about 600 for sometime and then decreased again. The most likely cause for the catalyst deactivation is the stable cobalt-carbon bond formed at the first period of the reaction and then reached equilibrium point. When the polymerization proceeds up to middle and high conversion, the chain transfer polymerization is further manipulated by diffusions of polymeric propagating chain and catalyst molecules, and the apparent chain transfer constant fell to value of below 300. It has been found also, that the data determined by the CLD equation are usually lower than those by the Mayo equation, especially at high conversion stage. It is because that both original equations are available for the instantaneous produced polymer or the case of very lower conversion stage. However, the GPC measurements give molecular weight distributions of the cumulated products rather than the instantaneous produced polymer. The number-average polymerization degrees for the instantaneous produced polymers were obtained from the GPC data, and used in the Mayo equation method together with the modification of the monomer concentration. It was believed that the apparent chain transfer constants from the modified Mayo equation method are more available for the middle and high conversion cases.

Consistent Determinations for the Diffusion and Reaction Rate Coefficients of Photoactive Monomers under Holographic Exposure

Analytical Rates Determinations And Simulations On Diffusion And Reaction Processes In Holographic Photopolymerization

Modeling for the Diffusion Limitation of Free Radical Polymerization

Simultaneous Measurement of Polymerization Kinetics and Stress Development in Radiation-Cured Coatings: A New Experimental Approach and Relationship between the Degree of Conversion and Stress

Numerical Simulation on Solvent Diffusion during Polymeric Coating Curing Processes

Cure Kinetics of an Epoxy Resin Containing Naphthyl/dicyclopentadiene Moieties and Bis‐phenoxy (3‐hydroxy) Phosphine Oxide System and Properties of Its Cured Polymer

THE EVOLUTION OF THE CHAIN TRANSFER CONSTANT DURING THE CATALYTIC CHAIN TRANSFER POLYMERIZATION OF 2-HYDROXYPROPYL METHACRYLATE

An Analysis of Photopolymerization Kinetics and Stress Development in Multifunctional Acrylate Coatings

Reactive Radical Facilitated Reaction-Diffusion Modeling for Holographic Photopolymerization

Monitoring and Optimization of the Synthesis Process of the Holographic Doped Photopolymers

Holographic Grating Formation in Cationic Photopolymers with Dark Reaction

Optimization of two-monomer-based photopolymer used for holographic recording

Cure kinetics study of the polymerization of N,N,N ' N '-tetrapropargyl-p,p '-diamino diphenyl methane with 1,1 '-bezidomethyl-4,4 '-biphenyl

High-density holographic recording parameters under different wavelength of a two dyes-sensitized photopolymer

Dual-Wavelength (UV and Blue) Controlled Photopolymerization Confinement for 3D-Printing: Modeling and Analysis of Measurements

Diffusion kinetics investigations of Nano Ag-doped holographic polymer dispersed liquid crystal gratings

Effect of Photo-Sensitizer and Thermo-Initiator Concentrations on Holographic Recording Performance of PQ/PMMA Photopolymer

Matrix Method for the Observation of Laser-Induced Photopolymerization with Short Time Curing

Dynamic Characterizations of High Diffraction Efficiency in Volume Bragg Grating Formed by Holographic Photopolymerization

Intermittent Curing and Its Effect on Pulsed Laser-Induced Photopolymerization

Determination of Propagation Rate Coefficients of 2‐hydroxyethyl Methacrylate in Aqueous Solution