Microstructure Evolution and Mechanical Properties of ZrC-added Nb–16Si–20Ti Alloys
Dezhi Chen,Qi Wang,Ruirun Chen,Zhecheng Zhou,Yanqing Su,Jingjie Guo,Hengzhi Fu
DOI: https://doi.org/10.1016/j.msea.2021.142159
IF: 6.044
2021-01-01
Materials Science and Engineering A
Abstract:The effect of ZrC addition on the phase composition, microstructure, and room-temperature mechanical prop-erties of arc melted Nb-Si-Ti based alloys has been systematically investigated. The results indicated that the addition of ZrC promotes the decomposition of (Nb,X)(3)Si phase. The addition of ZrC promotes the microstructure transformation from hypoeutectic to hypereutectic, and the eutectoid reaction of (Nb,X)(3)Si to Nbss/(Nb,X)(5)Si-3 eutectic structure. The KQ value of Nb-16Si-20Ti-1ZrC alloy is the highest, reaching 13.9 MPa m(1/2). The decomposition of (Nb,X)(3)Si phase can increase the room-temperature fracture toughness. However, the pre-cipitation of primary gamma-(Nb,X)(5)Si-3(g-b) phase deteriorates the room-temperature fracture toughness. Meanwhile, the more the content primary gamma-(Nb,X)(5)Si-3(g-b) is, the lower the room-temperature fracture toughness is. The maximum compressive strength of Nb-16Si-20Ti-1ZrC alloy is 2331 MPa, and the fracture strain of Nb-16Si-20Ti-3ZrC alloy is 11.4%. The fracture morphology of Nb-16Si-20Ti based alloys with ZrC additions is a brittle quasi-cleavage fracture.