Abstract:ZnS and Sm 3+ -doped ZnS nanoparticles (NPs) in silicate glasses were prepared by sol-gel technique. X-ray diffractometer (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and photoluminescence (PL) emission spectra were used to analyze the sample's morphology and crystal structure. UV–visible absorption spectra and PL emission spectra were used to look at the sample's optical characteristics. The formation of NBO and the elimination of the OH-group are confirmed by the FTIR spectra analysis. The XRD, SEM and TEM measurements confirmed that our glass sample is a nano-crystal. Optical absorption spectra have been used to evaluate three phenomenological Judd-Ofelt (JO) parameters Ω λ (λ = 2, 4, 6) to determine the local structure and bonding surrounding Sm 3+ ions. Glasses containing SSZ5 are found to have the highest parameter Ω 2 , which shows the covalency of the Sm-O bond, followed in decreasing order by glasses containing SSZ3 and SSZ1. This result implies that the coordination environment surrounding the Sm 3+ ions site is less centro-symmetric and more asymmetric in glass containing ZnS. For the glasses under investigation, the covalent character of the Sm-O bond is shown by the positive values of the bonding parameter δ. Four emission bands were seen in the PL spectra obtained at an excitation wavelength of 450 nm. Glass samples containing SSZ5 are shown to have greater radiative characteristics, such as branching ratio (β R ) and stimulated emission cross-section (σ), as well as potential emission band intensity. However all other prepared glasses, however, have been shown to be efficient lasing materials, indicating their appropriateness for the development of photonic materials that emit radiations in the range of blue to white regions. The Figure of Merit (FOM) results suggest that the prepared glasses might be used as optical amplifiers.

Preparation and characterization of ZnSe/5B2O3-95SiO2 nanocomposites

Synthesis of Two-Dimensional Micron-Sized Single-Crystalline ZnS Thin Nanosheets and Their Photoluminescence Properties

Sol–gel preparation of Ge nanocrystals embedded in SiO2 glasses

Photoluminescence Property of ZnO–SiO2composites Synthesized by Sol–gel Method

Structure and Photoluminescence of Ge Nanoparticles Embedded in SiO2 Gel Glasses Fabricated at Different Temperatures

Photoluminescence of Ge Nanoparticles Embedded in Sio2 Glasses Fabricated by A Sol-Gel Method

Preparation and Characterization of Na-doped ZnO Thin Films by Sol–gel Method

Fabrication and optical properties of mesoporous ZnSe nanosheets@SiO2 nanocomposites

Fabrication and Visible Emissions of ZnO Nanocrystal Doped Transparent Zinc Silicate Glass-Ceramics

Preparation and Characterization of Silica-Coated ZnSe Nanowires with Thermal Stability and Photoluminescence.

Preparation and optical properties of ZnO/ZnS heterostructured nanomaterials

Preparation and Characterization of ZnO-B2O3-SiO2 by Sol-Gel Method

Studies of synthesis and optical properties of ZnS nanocrystals

Preparation and characterization of ZnO-B2O3-SO2 by sol-gel method

Zns/Si Composite Nano-Structured Thin Films and Their Photoluminescence

Synthesis and Characterization of Zinc Sulfide/Polyvinyl Alcohol Nanocomposite Films

The synthesis and photocatalytic activity of ZnSe microspheres.

Nano polycrystalline structured ZnSe synthesized by the hydrothermal elemental-direct-reaction method: Structures, Raman and photoluminescence properties

The Thermal Stability and Photoluminescence of ZnSeO3 Nanocrystals Chemically Synthesized into SiO2/Si Track Templates

Effect of ZnS nanoparticles on the optical properties of Sm 3+ ions in silicate matrix

Radiative recombination in zinc blende ZnSe nanocrystals ion-beam synthesized in silica