Abstract:The plasma sprayed Fe-based Ni/WC composite coating on the surface of 45 steel was post-treated by laser remelting with the addition of nano-SiC. The effect of laser power on the interface microstructure of a laser remelting nano-SiC modified Fe-based Ni/WC composite coatings were researched. The metallographic structure, microscopic morphology, phase composition, and microhardness of the remelted layer were visually analyzed by metallographic microscope, scanning electron microscope (SEM), X-ray diffractometer (XRD), and microhardness tester, respectively. The results showed that the nano-SiC modified remelted coating was smooth and compact, and with no fine cracks. The remelted layer was mainly composed of [Fe,Ni], Cr, Fe0.04Ni0.36 phase. The metal elements Fe, Ni, Cr, and Si, and non-metallic element C, appeared to diffuse, and there was metallurgical bonding between the coating and the matrix. With the increase of laser power, the smaller the average grain size, the wider the half-peak height (FWHM), and the more obvious the grain refinement. When the laser power was 500 W, the interface metallurgical showed the best effect. Furthermore, the nano-sized SiC particles served as the core of the heterogeneous nucleation to refine the grains on the one hand, and promoted the formation of a hard intermediate phase in the coating on the other hand. Therefore, the laser remelting and the addition of nano-SiC particles greatly improved the microhardness of the coating. The larger the laser power, the smaller the microstructure characteristics and the fewer the number of holes. With increasing laser power, the hardness increased in general terms and the maximum hardness increased by 51%.

Laser remelting of plasma-sprayed yttria partially stabilized zirconia coatings

Laser Remelting of Plasma Sprayed Nicraly and Nicraly-Al2o3 Coatings

Laser Remelting of Plasma Sprayed Coatings

Preparation and Solid Particle Erosion Behaviors of Plasma-Sprayed and Laser-Remelted ZrO2-7wt.%Y2O3 Thermal Barrier Coatings

Glass phase microstructure and mechanical behaviors of laser-remelted Ni30Cr25Al15Co15Mo5Ti5Y5 coating reinforced by α/γ-Al2O3 phase

Microstructure and tribological properties of laser cladded TiAlSi composite coatings reinforced by yttria-stabilized zirconia

Femtosecond laser polishing yttria-stabilized zirconia coatings for improving molten salts corrosion resistance

Improving Molten CMAS Resistance of Thermal Barrier Coatings by Modified Laser Remelting Method

Effects of Laser Remelting on Microstructural Characteristics and Hot Corrosion Behavior of MСrAlY Coating Prepared by Plasma Spraying

Microstructure and Tribological Properties of Laser-Remelted Ni-Based WC Coatings Obtained by Plasma Spraying

Effect of laser remelting on the tribological performance of thermal barrier coatings

Alumina–zirconium ceramics synthesis by selective laser sintering/melting

Regulation of hydrophobicity on yttria stabilized zirconia surface by femtosecond laser

Very low-pressure plasma-sprayed dense yttria-stabilized zirconia coatings using an axial bi-cathode plasma torch

Effect of laser remelting on the microstructure and properties of the aluminum high silicon alloy coating

Mierostrueture and Performance of Plasma Sprayed Nano Zireonia Coating

The Effect of In Situ Laser-Assisted Plasma Spraying on the Plasma Etching Resistance of Yttrium Oxide Coating

Oxidation behavior of laser remelted plasma sprayed NiCrAlY and NiCrAlY–Al2O3 coatings

Effect of laser remelting on microstructure and properties of two Ni-base coatings by supersonic particles deposition

The Effect of Laser Power on the Interface Microstructure of a Laser Remelting Nano-SiC Modified Fe-Based Ni/WC Composite Coating

Ablation Behavior of Plasma-Sprayed La1-xSrxTiO3+δ Coating Irradiated by High-Intensity Continuous Laser