Abstract:The two kinds of flower-like ultrafine cobalt particles were prepared by reducing cobalt chloride (CoCl2·6H2O) with hydrazine hydrate (N2H4·H2O) under ultrasonic and microwave radiation, in which ethanol-water or ethylene glycol-water mixture was used as solvent. The morphology, crystal structure and magnetic properties of the as-prepared particles were characterized by scanning electron microscope (SEM), x-ray diffraction pattern (XRD) and vibrating sample magnetometer (VSM). The results show that the petals of the flower-like cobalt particles prepared in the ethanol-water system were dendritic, while the petals of the flower-like cobalt particles prepared in the ethylene glycol-water system were sword-like. The crystal structure of cobalt particles prepared in the two kinds of systems both consisted of hexagonal close-packed cubic phase and face-centered cubic phase, but the relative content was different. The saturation magnetization of the cobalt particles with dendritic petals and the cobalt particles with sword-like petals was the same approximately, but their coercivity was greatly different (the difference in value about 7184.14Am-1), which might be attributed to the magnetocrystalline anisotropy and shape anisotropy.

Metallic Cobalt Microcrystals with Flowerlike Architectures: Synthesis, Growth Mechanism and Magnetic Properties

Synthesis and Characterization of Metallic Co with Different Hierarchical Structures Prepared by A Simple Solvothermal Method

Fabrication and Magnetic Properties of Cobalt Microcrystals

Designed Synthesis and Magnetic Properties of Co Hierarchical Nanostructures

Highly Ordered Snowflakelike Metallic Cobalt Microcrystals

Synthesis of Flower-Like Co Microcrystals Composed of Co Nanoplates in Water/Ethanol Mixed Solvent

Controlled Synthesis and Morphology-Dependent Electromagnetic Properties of Hierarchical Cobalt Assemblies

Crystallization kinetics and magnetic properties of Fe 63.5Co10Si13.5B9Cu 1Nb3 nanocrystalline powder cores

Controlled Synthesis of Cobalt Flowerlike Architectures by A Facile Hydrothermal Route

Magnetic Properties and Morphology of the Cobalt Particles Prepared in Different Liquid Solvent

Synthesis and Characterization of Novel Three-Dimensional Metallic Co Dendritic Superstructures by a Simple Hydrothermal Reduction Route

Facile Route to Preparation of Fe-Co Microclusters with Highly Enhanced Magnetic Performances

Flowery ni microcrystals consisting of star-shaped nanorods: Facile synthesis, formation mechanism and magnetic properties

Facile Synthesis of Metallic Co Hierarchical Nanostructured Microspheres by a Simple Solvothermal Process

Manipulation of Morphology and Magnetic Properties in Cobalt Nanowires

Flower-like cobalt nanocrystals by a complex precursor reaction route

Self-Assembled Two-Dimensional Structure of Magnetic Cobalt Nanocrystals

Enhanced static magnetic properties, multiresonance behaviour and novel frequency-selective surface absorption properties of hierarchical flower-like hexagonal close-packed Co superstructures

Synthesis of Co submicrospheres self-assembled by Co nanosheets via a complexant-assisted hydrothermal approach

Hydrothermal Synthesis of Cobalt Particles with Hierarchy Structure and Physicochemical Properties

Selective-precursor reducing route to cobalt nanocrystals and ferromagnetic property