Abstract:The CdS nanowires were synthesized by a solvothermal method in ethylenediamine solvent both at short time (2 h) and longer time (more than 12 h). The nanowires had an average diameter of ca. 26 nm with a length of ca. 1-3 mu m at 200 degrees C for 2 h and similar to 43 nm in diameter and similar to 4-6 mu m in length at 200 degrees C for 12 h, respectively. These CdS nanowires were in crystalline wurtzite structure, and their crystal growth direction was [0001]. An interesting phenomenon was found that the nanowires synthesized at 2 h broken into nanorods with increasing reaction time. These broken nanorods grew into nanowires at 12 h again. More than 12 h, the diauxic growth nanowires become longer and little thicker without other obvious changes. Based on a series of experimental results, it was revealed that the formation of CdS nanowires followed a novel diauxic growth processes during the hydrothermal synthesis: (1) the formation of nanowhiskers on chrysanthemum-like nanostructure as seeds for 1-D nanostructure, (2) transformation of nanowhiskers into the CdS nanorods on the surface of chrysanthemum-like nanostructures, (3) growth of CdS nanowires from CdS nanorods, (4) broken of CdS nanowire into short CdS nanorods and (5) diauxic growth of CdS nanowires from CdS nanorods preferentially along the c-axis again.

Ligand-Assisted Solvothermal Growth of Cds Nanowires

Solvothermal Synthesis and Characterization of Uniform CdS Nanowires in High Yield

Diphenylthiocarbazone (Dithizone)-Assisted Solvothermal Synthesis and Optical Properties of One-Dimensional Cds Nanostructures

Solvothermal Synthesis of CdS Nanowires in a Mixed Solvent of Ethylenediamine and Dodecanethiol

Synthesis of Single Crystalline CdS Nanorods by a PVP-assisted Solvothermal Method

Nonaqueous Synthesis of CdS Nanorod Semiconductor

Good Optical Properties of Branched CdS Nanoparticles and Its Large Area Growth via Solvothermal Route

Effect of Solvents on Morphology and Size of CdS Nanoparticles via a Solvothermal Route

Synthesis of Single Crystalline CdS Nanowires with Polyethylene Glycol 400 As Inducing Template

High Yield CdS Nanowires Synthesized by Solvothermal Routes and Novel Diauxic Growth Mechanism

Rapid elongation of CdS nanowire at room temperature

Phase and Shape Evolution of Cds Nanocrystallites under Solvothermal Conditions

Novel regrowth mechanism of CdS nanowire in hydrothermal synthesis

Surfactant–ligand Co-Assisted Solvothermal Technique for the Synthesis of Different-Shaped CdS Nanorod-Based Materials

Effects of Preparation Parameters on One-Dimensional Cds Nanostructures by Diphenylthiocarbazone-Assisted Solvothermal Method

Single crystalline CdS nanorods fabricated by a novel hydrothermal method

Solvothermal Route to Semiconductor Nanowires

A chemical solution transport mechanism for one-dimensional growth of CdS nanowires

Synthesis of uniform CdS nanowires in high yield and its single nanowire electrical property

Shape-Controlled Synthesis Of Cds Nanocrystals In Mixed Solvents

Controlled Synthesis of CdE (E = S, Se and Te) Nanowires