Promotional Effect of Spherical Alumina Loading with Manganese-Based Bimetallic Oxides on Nitric-Oxide Deep Oxidation by Ozone
Fawei Lin,Zhihua Wang,Jiaming Shao,Dingkun Yuan,Yong He,Yanqun Zhu,Kefa Cen
DOI: https://doi.org/10.1016/s1872-2067(17)62860-2
2017-01-01
Abstract:Nitric oxide (NO) deep oxidation to dinitrogen pentoxide (N2O5) by ozone together with wet scrubbing has become a promising technology for nitrogen-oxide (NOx) removal in industrial boilers. Catalysts were introduced to enhance the N2O5 formation rate with less ozone injection and leakage. A series of monometallic catalysts (manganese, cobalt, cerium, iron, copper, and chromium) as prepared by the sol-gel method were tested. The manganese oxides achieved an almost 80% conversion efficiency at an ozone (O3)/NO molar ratio of 2.0 in 0.12 s. The crystalline structure and porous parameters were determined. The thermodynamic reaction threshold of NO conversion to N2O5 is oxidation with an O3/NO molar ratio of 1.5. Spherical alumina was selected as the support to achieve the threshold, which was believed to improve the catalytic activity by increasing the surface area and the gas-solid contact time. Based on the manganese oxides, cerium, iron, chromium, copper, and cobalt were introduced as promoters. Cerium and iron improved the deep-oxidation efficiency compared with manganese/spherical alumina, with less than 50 mg/m3 of outlet NO + nitrogen oxide, and less than 25 mg/m3 of residual ozone at an O3/NO molar ratio of 1.5. The other three metal oxides inhibited catalytic activity. X-ray diffraction, nitrogen adsorption, hydrogen temperature-programmed reduction, and X-ray photoelectron spectroscopy results indicate that the catalytic activity is affected by the synergistic action of NOx oxidation and ozone decomposition.