Abstract:The characteristics of low platinum Pt–BaO catalysts for NOx storage and reduction (NSR) were studied over three series of samples that have similar barium loadings (ca. 15wt% Ba), namely, Pt–BaO/Al2O3, CoOx promoted Pt–BaO/Al2O3 and Pt–BaO/ZrO2–Al2O3 catalysts. The catalysts were calcined at 800°C and their NSR performances were evaluated under cyclic lean (1000ppm NO and 10vol% O2 in Ar)/rich (1vol% H2 in Ar) conditions with particular attention paid to detect the possible harmful by-products, i.e., NH3 and N2O, during the reduction of the stored NOx under the rich condition. Lowering the Pt loading in the Pt–BaO/Al2O3 catalyst from 1.0 to 0.5wt% resulted in a 15% decrease in the NOx storage capacity (NSC) under the lean condition but the N2 selectivity under the rich condition declined dramatically (from 85% to 53%), indicating that the NOx reduction performance under the rich condition is the key to low platinum NSR catalysts. The cobalt oxides was identified as an unsuitable promoter for lowering the Pt loading; its addition into Pt–BaO/Al2O3 at the Pt loading of 0.5wt% further reduced the N2 selectivity under the rich condition although significant improvement in the NSC under lean condition could be observed. It was found instead that the use of ZrO2–Al2O3 as an alternative of the Al2O3 support was effective in lowering the dependence on Pt loading of the Pt–BaO for the NSR catalysis since the ZrO2–Al2O3 support could make the catalyst highly selective for the formation of N2 under the rich condition, at a lower Pt loading. The overall NSR performance of a Pt–BaO/ZrO2–Al2O3 catalyst with 0.5wt% Pt was found comparable to that of its counterpart Pt–BaO/Al2O3 catalyst with 1.0wt% Pt, demonstrating a viable way for developing low platinum NSR catalysts.

NOx Storage Performance at Low Temperature over Pt/BaO/Al_2O_3 by Plasma Treatment

Catalytic performance of MnO 2-CeO 2/Ti 0.25Zr 0.25Al 0.5O 1.75 monolith catalyst for low temperature selective catalytic reduction of NO with NH 3

Non-thermal plasma-assisted catalytic NOx storage over Pt/Ba/Al2O3 at low temperatures

Optimization for Plasma-facilitated Catalytic Reduction of NO_x

Nox Storage Capacity Enhancement on NiO/Al2O3 Pretreated with a Non-thermal Plasma

Role of Nitrogen-Containing Organic Compound in Plasma Exhaust Treatment

Combination of Nonthermal Plasma and Low Temperature-C3h8-Selective Catalytic Reduction over Co-In/H-Beta Catalyst for Nitric Oxide Abatement

Characterization of Al2O3 Supported Nickel Catalysts Derived from RF Non-thermal Plasma Technology

The Non-Thermal Plasma-Assisted Catalytic Conversion of NO under Low-Temperature

NO_x AOSORPTION ON NiO/γ-Al_2O_3 CATALYST AT LOW TEMPERATURE

Effects of Pd Doping on N2O Formation over Pt/BaO/Al2O3 During NO X Storage and Reduction Process

Characterization and Performance of Pt/SBA-15 for Low-Temperature SCR of NO by C3H6

Cold Plasma-Assisted Selective Catalytic Reduction of NO over B2O3/γ-Al2O3

Performance Improvement of NO x -Storage BaO/Al 2 O 3 by Using Barium Peroxide as the Precursor of BaO

Plasma-Assisted Catalytic Oxidation for Nitrogen Oxides Abatement

Enhancement of NO2 adsorption performance during adsorption-regeneration cycles over Pt/Ba/Al2O3 catalyst

Removal of NO by CH4 Using CuO/TiO2-γ-Al2O3 Catalyst in Combination with Plasma

Characteristics of low platinum Pt–BaO catalysts for NOx storage and reduction

Preparation of Pt-Pd/BaO/TiAlO catalyst for NOx storage-reduction and its sulfur resistance

Removal of NO by CH4 using CuO/TiO2-gamma-Al2O3 catalyst in combination with

Nonthermal-Plasma-Assisted Selective Catalytic Reaction Of No By Ch4 Over Cuo/Tio2/Gamma-Al2o3 Catalyst