Removal of NO by CH4 Using CuO/TiO2-γ-Al2O3 Catalyst in Combination with Plasma

Hui-Juan LI,Xiao-Yuan JIANG,Hui LIN,Xiao-Ming ZHENG

DOI: https://doi.org/10.3321/j.issn:0251-0790.2008.07.022

2008-01-01

Abstract:Cu-based catalysts supported on 15%TiO2/γ-Al2O3 carrier, was prepared by precipitation method. BET and XRD results show that the pore size distributions of 15%TiO2/γ-Al2O3 were mainly between micro-pores and meso-pores, and the CuO crystal diffraction peaks were detected, respectively. By using a hybrid system integrating plasma activation and a 12%CuO/TiO2/γ-Al2O3 catalyst, the reactions of NO+CH4+O2 were studied under different conditions including plasma only, catalyst only and plasma with catalyst. It is found that only plasma existed, the NO and CH4 conversion increased with a higher plasma power supply, and the addition of 2.5%O2 increased NO and CH4 conversion. Only when catalysts eristed, the NO and CH4 conversion both increased with the increase of temperature and reached 30% and 20%, respectively. And at the same time, the NO conversion was increased first with O2 content increasing and then decreased, and CH4 conversion was increased with O2 content increasing. When both plasma and catalyst coexisted, the conversion trend of the NO and CH4 with variation of O2 content was consistent with that when only catalyst existed. Besides, the NO conversion was in the range from 15% to 35% and the low temperature NO conversion was obviously increased. For the CH4 conversion, it was increased greatly to 90% .