Strengthening the Mechanical Properties of Unsaturated Polyester Resin Composite by Using SiC Particle

赵泉林,贾志军,李晓刚,叶正芳

DOI: https://doi.org/10.3969/j.issn.1002-7432.2010.02.006

2010-01-01

Abstract:The effects of SiC particle content and size on the mechanical properties of SiC/unsaturated polyester resin (UP)composite were studied by using universal testing machine and hardness meter.The fracture surface morphology of the tensile sample was observed.The results showed that the tensile strength of the UP compsite with 10 wt% SiC reached the maximum and the tensile strength of the systems with 8 000 mesh SiC and 1 000 mesh SiC were 53.2 MPa and 44.8 MPa respectively and increased by 68.1%,41.5% compared to that of pure resin systems.The elastic modulus and hardness of the systems with 30 wt% SiC were increased no less than 25.8% and 2.3% respectivly.The particle size had littele effect on the elastic modulus and hardness.The failure mode of the SiC/UP composite was brittle failure.