Effect of Composition on Sintering, Crystallization Behavior and Properties of CaO-Al2O3-SiO2 System Glass

陈国华,唐林江,职利,成钧,刘心宇

2009-01-01

Journal of Central South University

Abstract:Glass-ceramics with main crystalline phases of anorthite were prepared by sintering method.The effect of glass composition on sintering and crystallization behavior as well as properties of the glasses were investigated by using differential thermal analysis(DTA),X-ray diffraction(XRD),scanning electron microscopy(SEM)and property measurements.The results show that the increase of CaO content decreases the glass transition temperature(Tg)and the crystallization peak temperature(Tp)of anorthite-based glasses and makes the crystallization exothermic peak sharp.The crystallization activation energy of the glasses decreases and the glass crystallization improves with the increase of CaO content.The glass transition temperature(Tg)and the crystallization peak temperature(Tp)shift to high temperature and the glass crystallization becomes hard with the increase of SiO2 content.The sintering temperature of the glass samples reduces with the increase of CaO contents.Whereas,overfull CaO content will improve the precipitation of Ca2SiO4 phases and enhance the dielectric constant and the thermal expansion coefficient of samples.On the other hand,the increase of SiO2 content can lead to the thermal expansion coefficient to decrease and the dielectric properties of glass-ceramics improve.The prepared glass-ceramics exhibit high relative density(≥98.3%),moderate dielectric constant(6.9 7.5),low dielectric loss(≤0.1%),low thermal expansion coefficient(3.8×10 6 4.5×10 6/℃),low sintering temperature(900 1 000℃)and low temperature coefficient of dielectric content(66×10 6 113×10 6/℃),as well,which can be applicable in the electronic packaging field.