Abstract:Silicon oxynitride (SiON) is an important material to fabricate micro-electro-mechanical system (MEMS) devices due to its composition-dependent tunability in electronic and mechanical properties. In this work, the SiON film with 41.45% silicon, 32.77% oxygen and 25.78% nitrogen content was deposited by RF magnetron sputtering. Two types of optimized micro-structures including micro-cantilevers and micro-rotating-fingers were designed and fabricated using MEMS surface micromachining technology. The micro-cantilever bending tests were conducted using a nanoindenter to characterize the Young's modulus of the SiON film. Owing to the elimination of the residual stress effect on the micro-cantilever structure, higher accuracy in the Young's modulus was achieved from this technique. With the information of Young's modulus of the film, the residual stresses were characterized from the deflection of the micro-rotating-fingers. This structure was able to locally measure a large range of tensile or compressive residual stresses in a thin film with sufficient sensitivities. The results showed that the Young's modulus of the SiON film was 122GPa and the residual stresses of the SiON film were 327MPa in the crystallographic orientation of the wafer and 334MPa in the direction perpendicular to the crystallographic orientation, both in compression. This work presents a comprehensive methodology to measure the Young's modulus and residual stresses of a thin film with improved accuracy, which is promising for applications in mechanical characterization of MEMS devices.

New Method to Determine Young’s Modulus of Micro Crystal Based on Raman Spectrometer

Measurement of Young's modulus and residual stress of silicon microstructures

A Method of Measuring Young's Modulus and Residual Stress in Typical MEMS Structures Using a Surface Profilometer

Determining Young's modulus via the eigenmode spectrum of a nanomechanical string resonator

Determination of Young's Modulus for Microcantilevers in Atomic Force Microscopy

Mems/Nems Mechanical Characterization on Different Thin - Film Materials by Scanning along Micro-Machined Cantilevers

A Method to Determine Young’s Modulus of Soft Gels for Cell Adhesion

Measurement of mechanical properties for MEMS materials

Young's Modulus Characterization of Nano-Level Silicon Nanomembrane

Young’s Modulus of Polycrystalline Titania Microspheres Determined by in Situ Nanoindentation and Finite Element Modeling

Measurement Of Young'S Modulus And Residual Stress Of Micromembranes

Young's modulus and corresponding orientation in β-Ga 2 O 3 thin films resolved by nanomechanical resonators

A Micro-Tensile Method for Measuring Mechanical Properties of Mems Materials

Reduction in Modulus of Suspended Sub-2 nm Single Crystalline Silicon Nanomembranes

Tunable Resonant Frequencies For Determining Young'S Moduli Of Nanowires

Mechanical characterization of biocompatible thin film materials by scanning along micro-machined cantilevers for micro-/nano-system

Micro-Raman measurement of thickness in microelectromechanical silicon structures

Recent Efforts in Modelling Combined Rate, Size and Thermal Effects on Single Crystal Strength

Accurate Young’s Modulus Measurement Based on Rayleigh Wave Velocity and Empirical Poisson’s Ratio

Temperature Dependence of Young's Modulus of Single-Crystal Diamond Determined by Dynamic Resonance

Characterization of the Young's Modulus and Residual Stresses for a Sputtered Silicon Oxynitride Film Using Micro-Structures