Abstract:Aim: To explore the degradation characteristics of composite of calcium polyphosphate fiber (CPPF), calcium phosphate cement (CPC) and micromorselized bone in vitro. Methods: The experiment was conducted in the Central Laboratory of Animal Experiment of the First Hospital Affiliated to Harbin Medical University from February to October 2005. 1 The rabbit iliac bone was made into micromorselized bone with the diameter of 300-500 μm. 2 Two groups of biochemical composite were made respectively according to the mass-ratios of CPPF/CPC/micromorselized bone at 1:4:4 (CPPF group/CPC group/micromorselized bone group) and that of CPC/micromorselized bone at 1:1 (CPC group/micromorselized bone group). 3 The porosity was calculated by studying the pore diameter of composite under scanning electron microscope. 4 In vitro experiment of degradation, two groups of composite were put into the phosphate buffered solution (PBS) (pH 7.4) respectively to study the changes in weight-loss ratio of composite in degradation liquid as well as the changes in pH value of degradation liquid and the biomechanical changes in composite at different time-points. Results: 1 Changes in porosity, pH value and mass of degradation of both kinds of composites: The porosity of composite of CPPF/CPC/ micromorselized bone was 72.1% with the pore diameter of 100-400, and the pH value was constant while degradation. The mass changed little within 4 weeks and decreased rapidly after the 4th week, which was 50% of the initial mass in the 12th week. The porosity of compound materials of CPC/micromorselized bone was 58.2% and was 50-300 μm in the gap diameter with slight changes in pH value, and the mass changed little within 6 weeks, which decreased rapidly after 6 week, and was 70% of the initial mass in the 12th week. 2 Biomechanical changes in composite of two groups in the degradation: the primary biomechanical strength was 9.28 MPa in CPPF/CPC/micromorselized bone and was 6.21 MPa in CPC/ micromorselized bone, and there was significant difference between them (P< 0.05). The strength of CPPF/CPC/micromorselized bone decreased slowly within 4 weeks, then decreased obviously after 4 weeks, which was 0.18 MPa in the 12th week, while the strength of CPC/micromorselized bone decreased symmetrically and was 0.24 MPa in the 12th week. Conclusion: The composite of CPPF/CPC/micromorselized bone is a new bone repair material, which is suitable for bone tissue engineering for its good characteristics of porosity, pore diameter and degradation.

Degradation Behavior of Chitosan-fiber/calcium Phosphate Cement Composite for Artificial Bone

Mechanical Properties and Degradation Properties in Vitro of Carbon Fiber Reinforced Hydroxyapatite/polylactide Composite

Research Progress on the Physicochemical Properties of Improved CPC

Degradation of bone repairing composite of calcium polyphosphate fiber, calcium phospate cement and micromorselized bone in vitro

Effects of adding resorbable chitosan microspheres to calcium phosphate cements for bone regeneration

Preparation and Properties of Calcium Polyphosphate-Based Composite Scaffold for Bone Tissue Engineering

Biodegradable Cements for Bone Regeneration

Study on the poly(methyl methacrylate-acrylic acid)/calcium phosphate cement composite bound by chelation with enhanced water absorption and biomechanical properties

Animal Implantation with a New Type of Chitosan Microspheres/calcium Phosphate Cement

A novel strategy for calcium magnesium phosphate/carboxymethyl chitosan composite bone cements with enhanced physicochemical properties, excellent cytocompatibility and osteogenic differentiation

Biodegradation behavior of chitosan/calcium phosphate composites

Hierarchically porous calcium phosphate scaffold with degradable PLGA microsphere network

Preferentially Biodegradable Gypsum Fibers Endowing Invisible Microporous Structures and Enhancing Osteogenic Capability of Calcium Phosphate Cements

3D-printed composite, calcium silicate ceramic doped with CaSO4·2H2O: Degradation performance and biocompatibility

Structure and Properties of Chitosan Derivatives Modified Calcium Polyphosphate Scaffolds

Degradation pattern of porous CaCO3 and hydroxyapatite microspheres in vitro and in vivo for potential application in bone tissue engineering

Degradability of Injectable Calcium Sulfate/Mineralized Collagen-Based Bone Repair Material and Its Effect on Bone Tissue Regeneration

Development of paste-like organic/inorganic artificial bones compatible with bone remodeling cycles, consisting of β-tricalcium phosphate, calcium sulfate hemihydrate, and poly(lactic-co-glycolic acid) particles

In Vivo Behavior of Composite of Chitosan Microspheres/Cpc

Controlled degradation of chitosan-coated strontium-doped calcium sulfate hemihydrate composite cement promotes bone defect repair in osteoporosis rats

In vitro degradation of self‐reinforced poly(lactic acid) with beta‐tricalcium phosphate composite prepared by equal channel angular pressing