Abstract:A ternary composite of poly(amino acid), hydroxyapatite, and calcium sulfate (PAA/HA/CS) was prepared using in situ melting polycondensation method and evaluated in terms of mechanical strengths, in vitro degradability, bioactivity, as well as in vitro and in vivo biocompatibility. The results showed that the ternary composite exhibited a compressive strength of 147 MPa, a bending strength of 121 MPa, a tensile strength of 122 MPa, and a tensile modulus of 4.6 GPa. After immersion in simulated body fluid, the compressive strength of the composite decreased from 147 to 98 MPa for six weeks and the bending strength decreased from 121 to 75 MPa for eight weeks, and both of them kept stable in the following soaking period. The composite could be slowly degraded with 7.27 wt% loss of initial weight after soaking in phosphate buffered solution for three weeks when started to keep stable weight in the following days. The composite was soaked in simulated body fluid solution and the hydroxyapatite layer, as flower-like granules, formed on the surface of the composite samples, showing good bioactivity. Moreover, it was found that the composite could promote proliferation of MG-63 cells, and the cells with normal phenotype extended and spread well on the composite surface. The implantation of the composite into the ulna of sheep confirmed that the composite was biocompatible and osteoconductive in vivo, and offered the PAA/HA/CS composite promising material for load-bearing bone substitutes for clinical application.

Biodegradation behavior of chitosan/calcium phosphate composites

In vitro study of the biphasic calcium phosphate/chitosan hybrid biomaterial scaffold fabricated via solvent casting and evaporation technique for bone regeneration

Biomineralization Behavior of Biomimetic Chitosan Rod

Biodegradation and Compressive Strength of Phosphorylated Chitosan/Chitosan/Hydroxyapatite Bio-Composites

Structure and Properties of Chitosan Derivatives Modified Calcium Polyphosphate Scaffolds

Study of the Mechanical Property of Magnetite/ Hydroxyapatite/ Chitosan Nano-Composite

Synthesis and Characterization of Macroporous Chitosan/calcium Phosphate Composite Scaffolds for Tissue Engineering.

Mechanical, Structural, and Biological Properties of Chitosan/Hydroxyapatite/Silica Composites for Bone Tissue Engineering

A novel strategy for calcium magnesium phosphate/carboxymethyl chitosan composite bone cements with enhanced physicochemical properties, excellent cytocompatibility and osteogenic differentiation

Preparation and Cell Compatibility of Chitosan-hydroxyapatite Composite for Bone Repair

Preparation and in vitro investigation of chitosan/nano-hydroxyapatite composite used as bone substitute materials

Biodegradation Performance of a Chitosan Coated Magnesium-Zinc-tricalcium Phosphate Composite As an Implant.

Chitosan-Based Biomimetically Mineralized Composite Materials in Human Hard Tissue Repair

3D-printed composite, calcium silicate ceramic doped with CaSO4·2H2O: Degradation performance and biocompatibility

Preparation and Properties of Calcium Polyphosphate-Based Composite Scaffold for Bone Tissue Engineering

Novel Injectable Calcium Phosphate/chitosan Composites for Bone Substitute Materials

Novel Mesoporous Hydroxyapatite/Chitosan Composite for Bone Repair

Degradation Behavior of Chitosan-fiber/calcium Phosphate Cement Composite for Artificial Bone

Mechanics, Degradability, Bioactivity, in Vitro, and in Vivo Biocompatibility Evaluation of Poly(amino Acid)/hydroxyapatite/calcium Sulfate Composite for Potential Load-Bearing Bone Repair

Porous Composite Calcium Citrate/polylactic Acid Materials with High Mineralization Activity and Biodegradability for Bone Repair Tissue Engineering

Preparation and Characterization of A Novel Composite Containing Carboxymethyl Cellulose Used for Bone Repair