Biocompatibility and Degradation of an Injectable Nano-Sized Composite Bone Substitute
GE Liang,GOU San-huai,YANG Si-chuan,WANG Shi-long
DOI: https://doi.org/10.3321/j.issn:0258-879x.2006.10.020
2006-01-01
Academic Journal of Second Military Medical University
Abstract:Objective:To evaluate the in vitro cytotoxicity,in vivo response and degradation of a new injectable nano-hydroxyapatite(n-HA)/calcium sulphate hemihydrate(CSH) bone substitute in rabbits and to discuss its possible bio-degeneration mechanism.Methods: Pure CSH,n-HA,10%n-HA+CSH,20%n-HA+CSH,and 40%n-HA+CSH(the last 3 containing 10%,20%,and 40% n-HA,respectively) were subjected to MTT assay for their in vitro cytotoxicities.20%n-HA+CSH was implanted into rabbits' muscle and bone defects in the right femur,and the general conditions of rabbits,the pathological and TEM manifestations of tissues,and the imaging alterations were all observed 5 days,2,3,4,6,8,and 12 weeks after implantation.Results: Test of cytotoxicity showed that the average cell proliferation rate was over 77% after treated with the solutions of 5 bone substitutes(P0.05),with the cytotoxicity being 0-1(non-toxic).No general reaction was found in rabbits implanted with 20%n-HA+CSH and the weight of animals increased steadily.20%n-HA+CSH implanted in the muscle underwent a layer-by-layer degradation from 5 days after implantation and was almost completely degraded after 8 weeks,with no fibrosis,calcification or ectopic ossification.H-E staining showed that at the early stage the degraded materials were surrounded and wrapped by inflammatory cells;the fibroblasts gradually turned into fibrous cells encircling the degraded material.TEM observations indicated that the degradation was characterized by a cytophagic process and no cytotoxic signs were found in the phagocytes after phagocytosis.X-ray examination showed new osteoid and premature trabeculae scattered over the defective region 6 weeks after implantation,and there was normal trabecular tissue 8-12 weeks later.Conclusion: 20%n-HA+CSH has no obvious in vitro cytotoxicity,but has good biocompatibility.The in vivo degradation of 20%n-HA+CSH may be mediated by cytophagic process in a layer-by-layer manner.It degrades completely within 8-12 weeks,which is suitable for bone regeneration.