Abstract:Aim: To explore the degradation characteristics of composite of calcium polyphosphate fiber (CPPF), calcium phosphate cement (CPC) and micromorselized bone in vitro. Methods: The experiment was conducted in the Central Laboratory of Animal Experiment of the First Hospital Affiliated to Harbin Medical University from February to October 2005. 1 The rabbit iliac bone was made into micromorselized bone with the diameter of 300-500 μm. 2 Two groups of biochemical composite were made respectively according to the mass-ratios of CPPF/CPC/micromorselized bone at 1:4:4 (CPPF group/CPC group/micromorselized bone group) and that of CPC/micromorselized bone at 1:1 (CPC group/micromorselized bone group). 3 The porosity was calculated by studying the pore diameter of composite under scanning electron microscope. 4 In vitro experiment of degradation, two groups of composite were put into the phosphate buffered solution (PBS) (pH 7.4) respectively to study the changes in weight-loss ratio of composite in degradation liquid as well as the changes in pH value of degradation liquid and the biomechanical changes in composite at different time-points. Results: 1 Changes in porosity, pH value and mass of degradation of both kinds of composites: The porosity of composite of CPPF/CPC/ micromorselized bone was 72.1% with the pore diameter of 100-400, and the pH value was constant while degradation. The mass changed little within 4 weeks and decreased rapidly after the 4th week, which was 50% of the initial mass in the 12th week. The porosity of compound materials of CPC/micromorselized bone was 58.2% and was 50-300 μm in the gap diameter with slight changes in pH value, and the mass changed little within 6 weeks, which decreased rapidly after 6 week, and was 70% of the initial mass in the 12th week. 2 Biomechanical changes in composite of two groups in the degradation: the primary biomechanical strength was 9.28 MPa in CPPF/CPC/micromorselized bone and was 6.21 MPa in CPC/ micromorselized bone, and there was significant difference between them (P< 0.05). The strength of CPPF/CPC/micromorselized bone decreased slowly within 4 weeks, then decreased obviously after 4 weeks, which was 0.18 MPa in the 12th week, while the strength of CPC/micromorselized bone decreased symmetrically and was 0.24 MPa in the 12th week. Conclusion: The composite of CPPF/CPC/micromorselized bone is a new bone repair material, which is suitable for bone tissue engineering for its good characteristics of porosity, pore diameter and degradation.

In Vitro and in Vivo Degradation of an Injectable Bone Repair Composite

Structure and Biocompatibility of an Injectable Bone Regeneration Composite.

Mechanical Properties and Degradation Properties in Vitro of Carbon Fiber Reinforced Hydroxyapatite/polylactide Composite

Degradability of Injectable Calcium Sulfate/Mineralized Collagen-Based Bone Repair Material and Its Effect on Bone Tissue Regeneration

Repair of Rat Calvarial Bone Defects by Controlled Release of Rhbmp-2 from an Injectable Bone Regeneration Composite

Assessing the Character of the Rhbmp-2- and Vancomycin-Loaded Calcium Sulphate Composites in Vitro and in Vivo.

In Vitro and in Vivo Degradation of Mineralized Collagen-Based Composite Scaffold: Nanohydroxyapatite/collagen/poly(l-Lactide).

The Preparation Andin VitroEvaluations of a Nanoscaled Injectable Bone Repair Material

Preparation and characterization of an injectable composite

In vivo assessment of bone repair by an injectable nanocomposite scaffold for local co-delivery of autologous platelet-rich plasma and calcitonin in a rat model

[Study on Injectable Bioactive Bone Repairing Material of Nano-Hydroxyapatite and Polyamide-66 Composite].

Degradation-Kinetics-Controllable and Tissue-Regeneration-Matchable Photocross-linked Alginate Hydrogels for Bone Repair

Accelerating Bone Regeneration in Cranial Defects Using an Injectable Organic-Inorganic Composite Hydrogel.

Degradation of bone repairing composite of calcium polyphosphate fiber, calcium phospate cement and micromorselized bone in vitro

The long-term behaviors and differences in bone reconstruction of three polymer-based scaffolds with different degradability

Injectable in Situ Shape-Forming Osteogenic Nanocomposite Hydrogel for Regenerating Irregular Bone Defects

In vitro degradation characteristics of photocrosslinked anhydride systems for bone augmentation applications

In Vitro and in Vivo Evaluation of Degradability of Hydroxyapatite Coatings Synthesized by Ion Beam-Assisted Deposition

Silk Fibroin-Alginate-Hydroxyapatite Composite Particles in Bone Tissue Engineering Applications In Vivo

An injectable and self-healing cellulose nanofiber-reinforced alginate hydrogel for bone repair

Injectable Biocomposites For Bone Healing In Rabbit Femoral Condyle Defects