Abstract:In this study, we investigated the evolution of grain structures and second phases of a Mg-9.5Gd-4Y-2Zn-0.3Zr alloy during two-stage deformation that took place in the metal during hot extrusion, as well as their effects on its mechanical properties. We found that the alloy exhibited a bimodal grain structure consisting of equiaxed dynamic recrystallized (DRXed) grains and elongated unDRXed grains. As the extrusion process progressed, DRX occurred on a large scale, resulting in an increase in the proportion of DRXed grains from 17.8% to 93.2%, and a reduction in average grain size from 80.3 mu m to 9.41 mu m. The grain orientation also underwent a transition from a single orientation of an extrusion direction (ED) parallel to <0001> (i.e. ED//<0001>) to mixed orientations of ED//<01-10> and ED//<0001>. The primary mechanism of dynamic recrystallization (DRX) during extrusion involved particle-stimulated nucleation (PSN) accompanied by both continuous and discontinuous DRX. The Mg-9.5Gd-4Y-2Zn-0.3Zr alloy mainly contained intergranular 18R-long period stacking order (LPSO) phases and intragranular 14H-LPSO. As the extrusion process progressed, 18R-LPSO changed from blocky to lamellar to accommodate deformation, and beta-Mg5(Gd,Y) phase particles dynamically precipitated along DRXed grain boundaries. The 14H-LPSO phase was found to be primarily distributed within coarse unDRXed grains. As deformation via extrusion progressed, the quantity of 14H-LPSO gradually decreased. Ultimately, with the gradual dissolution of Mg5(Gd,Y), 14H-LPSO reprecipitated within the recrystallized grain boundaries. As the extrusion process progressed, both the yield strength (YS) and elongation (EL) increased from 132.6 MPa to 287.6 MPa and from 10.8% to 15.5%, respectively. This was mainly attributed to the significant reduction in grain size and second phase size.

Superplasticity and Microstructure in Mg–Gd–Y–Zr Alloy Prepared by Extrusion

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Superplasticity and microstructure in Mg–Gd–Y–Zr rolled sheet

Superplastic Behavior of an Extruded Mg-Zn-Y-Zr Alloy

Superplastic Behavior and Microstructure Evolution of a Fine-Grained Mg-Nd-Zn-Zr Alloy Processed by Hot Extrusion

Bimodal Grain Structure, Phase Transformation, and Mechanical Properties of a Mg-Gd-Y-Zn-Zr Alloy During Hot Extrusion

Microstructure Evolution and Mechanical Properties of the Mg-Sm-Gd-Zn-Zr Alloy During Extrusion

Microstructures and Mechanical Properties of Mg-10Gd-3Y-2Zn-0.5Zr Alloy

Superplasticity of Mg-5.8Zn-1Y-Zr Alloy Sheet Fabricated by Combination of Extrusion and Hot-Rolling Processes

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion

Influence of Extrusion Ratio on Microstructure and Tensile Properties of Mg–Gd–Y–Zn–Zr Alloy

Microstructure and Mechanical Properties of Moderate-Speed Extrudable Mg-Gd-Sm-Zr Alloy

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Coarse-grained Superplastic Behavior and Microstructural Characterization of Mg-Gd-Y-Zr Hot-Rolled Sheet

High Performance Mg Alloy with Designed Microstructure and Phases

A High-Strength Extruded Mg-Gd-Zn-Zr Alloy with Superplasticity

Superplasticity of Mg-Gd-Y Alloy in Tensile Test at Elevated Temperature

Microstructure and Mechanical Properties of Extruded Mg–8.5Gd–2.3Y–1.8Ag–0.4Zr Alloy

Microstructure and Mechanical Properties of Extruded Mg–Gd–Y–Zn Alloy with Mn or Zr Addition

Microstructure evolution during superplastic deformation process and its impact on superplastic behavior of a Mg-Gd-Y-Zn-Zr alloy

Recrystallization and Microstructural Evolution During Hot Extrusion of Mg 97 Y 2 Zn 1 Alloy