Abstract:Coal tar pitch was ground into powder and hydroformed with high pressure. After pre-oxidation, the pitch was activated by CO2 at high temperature. The effects of different preparation conditions on the yield, pore structure and phenol adsorption capacity of activated carbon were investigated, and activated carbon prepared under suitable conditions had good adsorption performance. A pore volume of 1-10 nm is the main absorption structure according to the analysis of pore size distribution and phenol adsorption capacity. The activated carbon showed high mechanical strength through compressive strength tests. Graphite nanocrystals around 5 nm were observed in the TEM images, and it illustrates that grain refinement results in the high strength. These nanocrystal stacked structures are easier to make and enlarge pores by activation than graphite layer stacked structures. Surface functional groups are considered not to be the active sites of phenol adsorption as suggested by the results of FTIR and Boehm's titration, and acidic oxygen-containing functional groups are harmful to phenol adsorption, which happen to be removed in the reductive preparation atmosphere. The donor-acceptor complex mechanism can be ruled out, and the pi-pi interactions are considered the most likely mechanism. The Langmuir and Reach-Peterson models are better fitted to the adsorption isotherms. Adsorption kinetics fit the intraparticle diffusion model best. Comparison of different activated carbons shows that suitable pore size is important for phenol adsorption. Thermodynamic parameters demonstrate that the adsorption process is spontaneous and exothermic, and the entropy increases. Pitch-based high-strength columnar activated carbon is an effective and low cost adsorbent for phenol wastewater treatment. This carbon nanocrystal material also provides a new direction for catalyst carriers.

Preparation of Spherical Activated Carbon and Their Physicochemical Properties

Preparation and Characterization of Polymer-Based Spherical Activated Carbons

Study on Bamboo-Derived Activated Carbon As Catalyst Support

Preparation and Characterization of Highly Mesoporous Spherical Activated Carbons from Divinylbenzene-Derived Polymer by ZnCl(2) Activation.

Synthesis of Spherical Carbons Containing Titania and Their Physicochemical and Photochemical Properties

Tio2 Combining Spherical Activated Carbon Photocatalysts and Their Physicochemical and Photocatalytic Activity

Preparation, characterization and adsorption performance of high surface area biomass-based activated carbons

Preparation and Electrochemical Properties of PF-based Activated Carbon

Pore Structure Regulation and Electrochemical Performance Characterization of Activated Carbon for Supercapacitors

Preparation of Activated Carbon from Co-Pyrolysis Activation of Fly Ash and Biomass

Preparation of porous carbons from phenol–formaldehyde resins with chemical and physical activation

The Research Advance of Preparation Process and Surface Property of Coal Based Activated Carbon

Preparation and performance of coal-based activated carbon based on an orthogonal experimental study

A study on the preparation of pitch-based high-strength columnar activated carbon and mechanism of phenol adsorption from aqueous solution

Modification of the activation characteristics of phenolic resin-based activated carbon spheres by polymer-blending method

Preparation of High-Surface-Area Activated Carbon from Coconut Shell Fibers

A facile approach to the preparation of S-doped porous carbons for CO 2 adsorption

Preparation of Activated Carbon Microspheres from Phenolic Resin with Metal Compounds by Sub- and Supercritical Water Activation

Effect of Pore Structure on SO2Removal by Activated Carbons

Micro-mesoporous activated carbon simultaneously possessing large surface area and ultra-high pore volume for efficiently adsorbing various VOCs

Numerical analysis of the porous structure of spherical activated carbons obtained from ion-exchange resins