Investigation of the Mechanical Properties of a Pressure-sensitive Adhesive Part 4 Crosslink Dependence of Molecular Weight Distribution of Sol Fraction of Lightly-crosslinked Acrylic Copolymers
Yoshiaki URAHAMA,Junpei MURATA,Hajime KISHI
DOI: https://doi.org/10.11618/adhesion.56.48
2020-02-01
Journal of The Adhesion Society of Japan
Abstract:Crosslink dependence of molecular weight distribution of sol fraction of lightly-crosslinked butyl acrylate - acrylic acid copolymers were studied. The butyl acrylate / acrylic acid( 95 / 5 in weight) copolymers were synthesized using living radical polymerization. In the sol fraction of the low equivalent composition( ie. 0.001 eq. and 0.002 eq.) of the crosslinking agent, the fraction of the molecular weight distribution of 1,000,000 or more was increased. Simultaneously, the distribution in the low molecular weight region was reduced. Moreover, the molecular weight distribution of the sol fraction was assumed to be sum of 3 curves of normal( Gauss) distribution, then was quantitatively analyzed using multi-peak fitting method. As the results, next conclusions were clarified: 1. Dimerization occurred without gelation in the low equivalent composition, which made the fraction of the molecular weight distribution of 1,000,000 or more. 2. With increasing the cross-linking agent, the high molecular weight fraction was sequentially altered into gel fraction. Therefore, the high molecular weight distribution of the sol fraction rapidly decreased with increasing the gel formation.