Preparation of Low-shrinkage Polypropylene by Tailoring Crystallization
Ze-shuang Qiao,Fa-sheng Zou,Wen-bo Song,Hong-wei Bai,Qiang Fu
DOI: https://doi.org/10.11777/j.issn1000-3304.2022.22450
2023-01-01
Acta Polymerica Sinica
Abstract:Isotactic polypropylene (iPP) suffers from high mold shrinkage mostly associated with the crystallization-induced volume shrinkage during the melt-processing, which inevitably leads to an inaccurate size of final products. In this work, a facile and effective strategy based on the crystallization manipulation has been reported to address this issue. To do this, beta-nucleating agent (beta-NA) was utilized to tailor the crystalline structure and morphology of iPP. The effect of beta-form crystallization on the volume shrinkage, and linear shrinkage of injection-molded iPP products has been analyzed by differential scanning calorimetry (DSC), X-ray diffraction (XRD), polarized optical microscopy (POM), and scanning electron microscopy (SEM). The results show that, neat iPP can exclusively crystallize into alpha-form crystals upon non-isothermal melt-crystallization, whereas abundant beta-form crystals are induced by adding small amounts (0.05 wt%.0.5 wt%) of beta-NA. Moreover, with the increase of beta-NA content, the beta-crystalline morphology is found to change from typical spherulites to unique bundle-like crystals. Very interesting, the predominant formation of beta-form crystals can markedly reduce the shrinkage of the iPP products. Especially, when the fraction of beta-form crystals is increased from 3.6% to 90.6%, the linear shrinkage of the products is found to decrease from 1.7% to 1.2%, while their volume shrinkage declines from 12.2% to 10.6%. This finding is in good accordance with the theoretical calculation. Further analysis indicates that such beta-NA can self-organize into fibrillar crystals in iPP melts, which are prone to orientate along the flow direction and then induce the orientational crystallization of iPP chains, ultimately leading to the anisotropic shrinkage. Moreover, the shrinkage is heavily dependent on the fraction of beta-form crystals, rather than the crystalline morphology. This work could provide a guideline for the development of low-shrinkage iPP materials. [GRAPHICS] .