Abstract:The effect of minerals on the high-temperature graphitization process of coke was thoroughly investigated using by X-ray diffraction (XRD), Raman spectroscopy (Raman), scanning electron microscope (SEM), physical adsorption instrument, etc. The structure-activity relationship between the microstructure of coke-based graphite and lithium storage performances was identified. The findings demonstrate that the microstructure of coke-based graphite is related to the mineral content and the final graphitization temperature affects the Si or Fe catalytic graphitization of coke. The appropriate amount of minerals as the catalyst can reduce the interlayer spacing, improve the graphitization degree and increase the crystallite size of the coke graphitization sample. The catalytic graphitization of coke involves the carbide transition, which is further confirmed by XRD and SEM-EDS analysis. By proper adding the mineral to the coke during the graphitization process, it is clear that the electrochemical performances of the synthetic graphite as anode for lithium-ion batteries can be improved obviously. Coke-based graphite DCG-20Si-2800 and DCG-30Fe-2800 as anode material show good comprehensive electrochemical performances. And the reversible specific capacities of both at 0.1 C are as high as 353.9 mAh/g and 361.9 mAh/g, respectively, which are quite close to the theoretical capacity of graphite (1 C = 372 mAh/g). Thus, the study successfully reveals the law of mineral catalysis in the graphitization process of coke and demonstrates the feasibility of coke-based graphite products as anode material. It can be expected that coke can be useful sources of artificial graphite if the graphitization process is adequately improved.

Preparation of Graphitized Taixi Coal and Its Electrochemical Properties

Graphitization Mechanisms and Electrochemical Performance of Needle Coke Anode for Li-ion Battery

Surface Modifications of Carbon Materials Used As Anode of Lithium Ion BatteryⅡ.The Carbon Material with Core Shell Structure and Its Positive Effect on Cell Performance of Graphite Anode

Catalytic graphitization of coke and electrochemical performances of coke-based graphite

The charge-discharge properties of carbon materials prepared from coal for the anode of lithium ion batteries

Coal-derived Synthetic Graphite with High Specific Capacity and Excellent Cyclic Stability As Anode Material for Lithium-Ion Batteries

Hard Carbon Derived from Coal Tar Pitch for Use as the Anode Material in Lithium Ion Batteries

Solid-State Synthesis of Graphite Carbon-Coated Li4ti5o12 Anode for Lithium Ion Batteries

Highly graphitized coal tar pitch-derived porous carbon as high-performance lithium storage materials.

Carbon-coated Si-Cu/graphite Composite As Anode Material for Lithium-ion Batteries

Preparation and lithium storage of anthracite-based graphite anode materials

A comparison of the electrochemical performance of graphitized coal prepared by high-temperature heating and flash Joule heating as an anode material for lithium and potassium ion batteries

Preparation and Electrochemical Properties of Coal-Based Activated Carbons

A new strategy for preparation of high-performance onion-like anode material from coal tar pitch residue

Study on Carbon Prepared from Coal As Anode for Lithium Ion Battery

Preparation of coal gasification fine slag-based supercapacitive carbon using hydrothermal deashing and alkali activation

Stable cycling and low-temperature operation utilizing amorphous carbon-coated graphite anodes for lithium-ion batteries

Enhanced TiO2/SiCx Active Layer Formed In Situ on Coal Gangue/Ti3C2 MXene Electrocatalyst as Catalytic Integrated Units for Efficient Li-O2 Batteries

Catalytic Graphitization of Anthracite as an Anode for Lithium-Ion Batteries

Sub-millisecond lithiothermal synthesis of graphitic meso–microporous carbon

Mesoporous Tubes Composed of Graphitic Carbon-Doped Co 3 O 4 Nanoparticles for Lithium Storage