Synthesis of MnFe2O4 Nanofibres by Hydrothermal Method

HOU Xiang-yu,FENG Jing,WANG Zhi-qiang,LIU Xiao-han,ZHANG Mi-lin
2010-01-01
Abstract:A hydrothermal route without any surfactant or template was suggested to synthesize nanofibre MnFe2O4.XRD,Mssbauer,SEM and VSM were used to investigate the crystal structure,distribution of iron ions,morphologies and magnetic properties.Results showed that the products were pure phase spinel MnFe2O4 with a space group of Fd-3m.The distribution of iron ions on A and B sites were 41.3%and 58.7%.The morphology of MnFe2O4was uniform nanofibre with diameter of about 20nm.The ratio of length to diameter was up to 50and the surface was polish.The obtained MnFe2O4could be magnetized easily and showed a soft magnetism at room temperature with a high saturation magnetization(Ms=62.07A·m2/kg),low Mrand low Hc.