Technology for Electrodeposition of Zn-Ni-La Alloy Coating and Corrosion Resistance of the Coating

DONG Peng,ZHANG Ying-jie,FAN Yun-ying,LI Fu-shao

DOI: https://doi.org/10.16577/j.cnki.42-1215/tb.2008.11.024

2008-01-01

Abstract:The technology for electrodeposi-tion of Zn - Ni-La alloy coating from chloride baths was investigated,where rare earth La was introduced to reduce consumption of Ni. The effect of La and complexing agents on the composition and microstructure of the ternary alloy coating were investigated, while the corrosion resistance of the Zn - Ni - La alloy coating was evaluated as well. Results indicated that rare earth La helped to increase the cathode polarization potential of Zn-Ni-La coating by 0. 2 V and improve the compactness brightness of the coating as well. Moreover, the introduction of La also contributed to improve the anti-corrosion ability of the Zn-Ni-La coating. Besides, along with increasing concentration of complexing agents in the plating bath, the concentration of La in the ternary alloy coating first rose and then decreased, and it reached a peak level when the concentrationof the complexing agents was 20 g/L and 30 g/L. Also, the introduction of La in the ternary alloy coating led to a significantdecrease in the content of Ni, and the ternary alloy coating containing about 2% Ni had corrosion resistance comparable to that of Zn-Ni coating containing Ni as much as 13%.