Effect of Ti and Mg on the damping behavior of in situ aluminum composites

Yijie Zhang,Naiheng Ma,Haowei Wang,Yongkang Le,Songchun Li

DOI: https://doi.org/10.1016/j.matlet.2005.06.055

IF: 3

2005-01-01

Materials Letters

Abstract:Damping capacity of in situ TiB2 particulate reinforced aluminum composites with Ti and Mg excess were investigated. The composites were fabricated with an exothermic reaction process via K2TiF4 and KBF4 salts. The damping behavior of materials over a temperature range of 30–300 °C was investigated by using a dynamic mechanical thermal analyzer. Experimental findings indicate that the damping capacity of composites with Ti, Mg excess, respectively is lower than that of Al/5 wt.% composite when temperature is below 180 °C and is higher than of Al/5 wt.% composite above 180 °C. The main effects of these elements are the formation of thin layers on TiB2 particulates, which resulted in the change of damping capacity.