Cu-doped ZnO Thin Film Prepared by Metallorganic Chemical Vapor Deposition
XU Lu,LIANG Hong-wei,LIU Yuan-da,LI Chun-ye,LIU Yang,BIAN Ji-ming,LI Guo-xing,LI Wan-cheng,WU Guo-guang,DU Guo-tong
DOI: https://doi.org/10.3788/fgxb20113209.0956
2011-01-01
Abstract:Un-doped and Cu-doped ZnO thin films were grown on c-Al2O3 substrate by metalorganic chemical vapor deposition(MOCVD) system.The way of changing the temperature of Cu(tmhd)2 source bottle was used to change the saturated vapor pressure of Cu(tmhd)2,in the meantime to change the quantity of Cu(tmhd)2 carried into the the reaction chamber.Then the content of Cu in ZnO films was tested to study the effects of Cu doping on the luminescent properties of ZnO,and explore the process technique and condition of controlling Cu valence in ZnO films.X-ray diffraction(XRD) show un-doped ZnO and ZnO∶Cu samples have good c-axis preferred orientation growth.The Cu content of these samples were measured by X-ray photoelectron spectroscopy(XPS).The content of Cu in ZnO films were not increased when the Cu(tmhd)2 source temperature was increased,which indicated that increasing the Cu(tmhd)2 source temperature did not lead to any increase of the Cu-doping level,and the solubility of Cu ions in ZnO is quite low.Low-temperature photoluminescence(PL) measurements show a strong and broad blue-violet(BV) light emission peak ranging from 2.8 to 3.3 eV,which could be assigned to donor-acceptor pair(DAP) recombination(between unknown shallow donor level and Cu-related acceptor level).Temperature dependent PL show a red-shift of the BV emission with increasing the temperature from 10 to 180 K,and a new weak shoulder peak appearing at BV emission's high-energy side at 80 K,which could be assigned to eA0.Moreover,the decrease of Cu content in ZnO∶Cu film resulted in quenching the intensity of BV emission red-shift of BV emission's peak position.This phenomenon is interesting and rarely reported in the previous works.However,we still need further study to clarify that if it is the electron transition between Zni-related donor energy level and valence band that causes the BV emission.