Abstract:A new hyperbranched charring-foaming agent (PCAT) containing triazine and triazole groups was successfully synthesized and characterized, and its special pyrolysis behavior was analyzed. It was combined with PAPP as an acid source to form an intumescent flame-retardant system. The composite with 20% flame retardants containing PAPP/PCAT (3:1) showed better flame-retardant and smoke suppression properties. The LOI of the PP/PAPP/PCAT composite increased to 30.2% and achieved UL-94 V-0 rating when the mass ratio of PAPP/PCAT was 3:1. In cone calorimetry experiments, it was demonstrated to reduce PHRR and THR by 84.7% and 48.9%, respectively. Meanwhile, the PSPR and TSP were also reduced by 77.9% and 56.2%, respectively, relative to PP. This indicates that the PP modified by partially doping PCAT in PAPP has significantly enhanced heat dissipation and smoke suppression performance, thus performing higher fire safety. In terms of FRI, PP/PAPP/PCAT composite was considered to be of "good" flame retardancy. Thermal gravimetric analysis demonstrated that PCAT significantly improved the char yield of PP when combined with PAPP. The morphology and properties of the residue showed that PP/PAPP/PCAT could produce a significant expanded foam insulating carbon layer, and the graphitization degree of the residual carbon was enhanced. The investigation of their water resistance demonstrated that the PP/PAPP/PCAT composite still obtained a UL-94 V-0 rating after 168-h soaking in water.

Synthesis of Triazine-Based Macromolecule Charring Agent and Its Application to Polypropylene

The mechanical properties and thermal performances of polypropylene with a novel intumescent flame retardant

A Novel Halogen‐free Intumescent Flame Retardant Containing Phosphorus and Nitrogen and Its Application in Polypropylene Systems

Flame Retardation and Thermal Degradation of Intumescent Flame‐retarded Polypropylene Composites Containing Spirophosphoryldicyandiamide and Ammonium Polyphosphate

Synthesis of A Novel Charring Agent Containing Pentaerythritol and Triazine Structure and Its Intumescent Flame Retardant Performance for Polypropylene

Synthesis of a Novel Triazine-Based Polymeric Flame Retardant and Its Application in Polypropylene

Synthesis of a triazine charring agent containing hydroxyl and triazine ring and its flame retardant application in thermoplastic polyolefin

One-pot Synthesis of a Novel S-Triazine-based Hyperbranched Charring Foaming Agent and Its Enhancement on Flame Retardancy and Water Resistance of Polypropylene

Synthesis of a Novel Triazine-Based Hyperbranched Char Foaming Agent and the Study of Its Enhancement on Flame Retardancy and Thermal Stability of Polypropylene

Research on Synthesis of Charring Agent Containing Silicon and Its Application in Flame Retarded PP

Synthesis of a charring-foaming agent containing triazine and triazole groups and its flame retardancy in PP

Effect of char-forming agents rich in tertiary carbon on flame retardant properties of polypropylene

Synthesis of a Novel Hyperbranched and Phosphorus‐containing Charring‐foaming Agent and Its Application in Polypropylene

Effect of a bio-based copolymer containing lysine, dopamine and triazine on flame retardancy and mechanical properties of thermoplastic polyurethane/ammonium polyphosphate

Synthesis of a highly efficient charring agent and its application to intumescent flame‐retardant coatings for 3D‐printed polypropyleneparts

A novel highly efficient intumescent flame-retardant polypropylene: Thermal degradation, flame retardance and mechanism

Synthesis of a hyperbranched phosphorus-containing polyurethane as char forming agent combined with ammonium polyphosphate for reducing fire hazard of polypropylene

Cyclotriphosphazene-Based Intumescent Flame Retardant Against the Combustible Polypropylene

Synthesis and Application of a Mono-Component Intumescent Flame Retardant for Polypropylene

Synthesis of a Novel Intumescent Flame Retardant and Its Flame Retardancy in Polypropylene

Hyperbranched Phosphorus/nitrogen-Containing Polymer in Combination with Ammonium Polyphosphate As a Novel Flame Retardant System for Polypropylene