Abstract:In this work, a silicon‐, phosphorus‐, nitrogen‐containing flame retardant system was constructed via the combination of the caged organic octaphenyl silsesquioxane (OPS) and an intumescent flame retardant (IFR) composed of piperazine pyrophosphate and melamine polyphosphate. Compared with the IFR mixture alone, the designed OPS/IFR system simultaneously endowed polypropylene (PP) with a higher charring flame‐retardant effect and better mechanical properties under the same loading amount. With only 0.5 wt% OPS and 19.5 wt% IFR in PP, both 3.2 mm‐ and 1.6 mm‐thick flame‐retardant composite reached UL 94 V‐0 level, while the sample with IFR only passed the 3.2 mm‐thick UL 94 V‐0 rating. Moreover, compared with IFR, OPS/IFR with a specific mass ratio also performed higher limited oxygen indexes, improved anti‐dripping behavior in the glow‐wire test, and suppressed the heat and smoke release to a larger extent of PP composite. The main mechanism was that a phosphorus/silicon synergistic charring effect occurred in PP composites during the combustion, thus forming more compact char layers with rich phosphorus/silicon compounds. The investigation of the multielement OPS/IFR system also disclosed a more effective flame retardant working way in PP through synergistic charring effect. Meanwhile, due to the mico‐nanoscale dispersibility of OPS in PP, the constructed composites kept higher mechanical performances compared with the sample loaded with IFR alone.

Research on Synthesis of Charring Agent Containing Silicon and Its Application in Flame Retarded PP

Flame Retardation and Thermal Degradation of Intumescent Flame‐retarded Polypropylene Composites Containing Spirophosphoryldicyandiamide and Ammonium Polyphosphate

A Novel Halogen‐free Intumescent Flame Retardant Containing Phosphorus and Nitrogen and Its Application in Polypropylene Systems

Synthesis of A Novel Charring Agent Containing Pentaerythritol and Triazine Structure and Its Intumescent Flame Retardant Performance for Polypropylene

Synthesis of a charring-foaming agent containing triazine and triazole groups and its flame retardancy in PP

One-pot Synthesis of a Novel S-Triazine-based Hyperbranched Charring Foaming Agent and Its Enhancement on Flame Retardancy and Water Resistance of Polypropylene

Synthesis of a Novel Hyperbranched and Phosphorus‐containing Charring‐foaming Agent and Its Application in Polypropylene

Effect of char-forming agents rich in tertiary carbon on flame retardant properties of polypropylene

Small core of piperazine/silane aggregation initiate efficient charring flame retardant effect in polypropylene composites

Synergistic effect between a char forming agent (CFA) and microencapsulated ammonium polyphosphate on the thermal and flame retardant properties of polypropylene

Synthesis of a Novel Triazine-Based Hyperbranched Char Foaming Agent and the Study of Its Enhancement on Flame Retardancy and Thermal Stability of Polypropylene

Synthesis of a hyperbranched phosphorus-containing polyurethane as char forming agent combined with ammonium polyphosphate for reducing fire hazard of polypropylene

Synthesis of a highly efficient charring agent and its application to intumescent flame‐retardant coatings for 3D‐printed polypropyleneparts

Intumescent Flame-retardant Modification of Polypropylene/Carbon Fiber Composites

A novel highly efficient intumescent flame-retardant polypropylene: Thermal degradation, flame retardance and mechanism

Preparation and properties of bio-based intumescent flame retardant containing chitosan functionalized ammonium polyphosphate for polyurethane

Cage‐shaped octaphenyl silsesquioxane with micro‐nano dispersibility for strengthening intumescent flame retardancy in polypropylene composites

Preparation and characterization of multipurpose polypropylene composite with outstanding flame retardancy and antistatic property

Flame-retardant and thermal properties of highly efficient water-resistant intumescent flame-retardant polypropylene composites

Cyclotriphosphazene-Based Intumescent Flame Retardant Against the Combustible Polypropylene

Effect of phytic acid-modified layered double hydroxide on flammability and mechanical properties of intumescent flame retardant polypropylene system