Abstract:To enhance its properties, ammonium polyphosphate (APP) was subjected to modification using a synthesized phosphorus-containing silica gel, resulting in MAPP. Ammonium polyphosphate (APP) was modified by synthesized phosphorus-containing silica gel, resulting in MAPP, which was then used to form thermoplastic polyurethane composites. MAPP exhibited better thermal stability with a smaller dispersion size, lower initial decomposition temperature and better resistance to heat at high temperatures than APP. At the same time, MAPP showed more obvious advantages in improving the char yield, flame retardant performance and mechanical properties of TPU. TPU/5%MAPP showed a limiting oxygen index of 29.1% during burning tests, significantly better than TPU/5%APP (27.3%). The cone calorimeter test results also indicated that the incorporation of MAPP resulted in a significant reduction in key parameters such as peak heat release rate, total heat release, and total smoke release and an increase of the char yield of TPU composite. The TG result showed that the T max of the TPU/5%MAPP composite increased and the mass loss rate decreased compared with that of TPU/5%APP. Moreover, the tensile strength of the TPU/5%MAPP composite increased by 18.5% compared with the TPU/5%APP composite due to the improved dispersibility of MAPP than APP. An analysis of the fire resistance mechanism showed that the improved flame retardance in the TPU/5%MAPP composite resulted from the structural changes in the char residue. This study provides an efficient and extensible approach for the synthesis of high-performance flame retardant TPU materials.

Effect of a bio-based copolymer containing lysine, dopamine and triazine on flame retardancy and mechanical properties of thermoplastic polyurethane/ammonium polyphosphate

Synergism of triazine containing dopamine to flame retardancy, smoke suppression, and mechanical properties of thermoplastic polyurethane/ammonium polyphosphate

The preparation of ammonium polyphosphate@ nickel/cobalt-layered double hydroxide and its application as flame retardant in thermoplastic polyurethane

Highly efficient intumescent flame retardant of dopamine-modified ammonium polyphosphate for the thermoplastic polyurethane elastomer

Surface Modification of Ammonium Polyphosphate for Enhancing Flame-Retardant Properties of Thermoplastic Polyurethane

Cobalt ions loaded polydopamine nanospheres to construct ammonium polyphosphate for the improvement of flame retardancy of thermoplastic polyurethane elastomer

Effects of flame retardants integrated with citrate and ammonium polyphosphate on thermal stability and flame retardancy of thermoplastic polyurethane elastomer

Core-shell flame retardants based on Chitosan@MMT coated ammonia polyphosphate for enhancing flame retardancy of polyurethane

Cupric ion decorated ammonium polyphosphate as an effective flame retardant for thermoplastic polyurethane

The preparation of phosphorus and nitrogen-containing structure towards the enhancement of flame retardancy for thermoplastic polyurethane elastomer

Synergistic effects between iron-graphene and ammonium polyphosphate in flame-retardant thermoplastic polyurethane

Fire behavior and mechanical properties of phosphorus-containing silica gel coated ammonium polyphosphate as fire retardants in thermoplastic polyurethane (TPU)

Preparation of novel and efficient arylphosphonate flame retardants for simultaneously enhancement of fire safety and UV-shielding properties of transparent thermoplastic polyurethane

Design of novel double-layer coated ammonium polyphosphate and its application in flame retardant thermoplastic polyurethanes

Synthesis of a triazine charring agent containing hydroxyl and triazine ring and its flame retardant application in thermoplastic polyolefin

Copper metal‐organic framework toward flame‐retardant enhancement of thermoplastic polyurethane elastomer composites based on ammonium polyphosphate

Enhanced flame resistance and mechanical property of TPU with triazine silane coupling agent modified APP by wet ball milling

Biomass tannic acid intermediated surface functionalization of ammonium polyphosphate for enhancing fire safety and smoke suppression of thermoplastic polyurethane

Morphology-manipulated aluminum diethylphosphinate and flame-retardant properties in thermoplastic polyurethane

Effect carbon black microencapsulated ammonium polyphosphate on the flame retardancy and mechanical properties of polyurethane composites

Component ratio effects of melamine cyanurate and aluminum diethylphosphinate in flame retardant TPU