Abstract:In the past work, few study considers an effect of nanoparticle as a synergistic flame retardant on the interfacial interaction between flame retardants and polymer matrix, as well as further influence on the flame retardancy and mechanical properties of flame-retarding polymers. In this work, the electrostatic action was used to prepare a novel ammonium polyphosphate@layered double hydroxide (APP@LDH) in which the LDH nanoparticles accumulated at the surface of APP to achieve the highly-efficient synergistic action of LDH in thermoplastic polyurethane/APP (TPU/APP) and reduce the deterioration of APP to mechanical properties of TPU. Scanning electron microscope, etc., demonstrated that the APP@LDH was prepared successfully. Combustion tests results showed that the APP@LDH had much higher flame retarding efficiency than the APP/LDH which was prepared through a simple physical blending process. Only 1.0 wt% LDH made the TPU pass the V-0 rating with no dripping in the UL-94 test and a limiting oxygen index (LOI) of 29.2% in the case of 7.0 wt% APP@LDH. However, the TPU/APP/LDH with 1.0 wt% LDH did not pass the V-0 rating, and a dripping behavior also existed at 7.0 wt% APP/LDH. In cone calorimeter test, the heat release and smoke production of TPU/APP@LDH were also lower than the corresponding values of TPU/APP/LDH under equal amount of LDH. The analysis of flame-retardant mechanism proved that an enhanced condensed action induced by the interfacial LDH dominated the better flame retardance of APP@LDH system than that of APP/LDH system. Another important aspect is that the mechanical properties of APP@LDH system showed remarkable improvements in comparison with those of APP/LDH system. The tensile strength of TPU with 7.0 wt% APP@LDH was 32.5% higher than that of TPU with 7.0 wt% APP/LDH under equal 1.0 wt% LDH. Meanwhile, the elongation at break for the former was maintained at 863.0%, almost equal to that of TPU. This work illustrates that the interfacial accumulation of LDH may enhance its synergistic flame-retarding efficiency and meanwhile achieve the mechanical enhancement for TPU/APP. (C) 2019 Elsevier Ltd. All rights reserved.

The preparation of ammonium polyphosphate@ nickel/cobalt-layered double hydroxide and its application as flame retardant in thermoplastic polyurethane

Cupric ion decorated ammonium polyphosphate as an effective flame retardant for thermoplastic polyurethane

Cobalt ions loaded polydopamine nanospheres to construct ammonium polyphosphate for the improvement of flame retardancy of thermoplastic polyurethane elastomer

Design of novel double-layer coated ammonium polyphosphate and its application in flame retardant thermoplastic polyurethanes

Surface Modification of Ammonium Polyphosphate for Enhancing Flame-Retardant Properties of Thermoplastic Polyurethane

The preparation of phosphorus and nitrogen-containing structure towards the enhancement of flame retardancy for thermoplastic polyurethane elastomer

Highly efficient intumescent flame retardant of dopamine-modified ammonium polyphosphate for the thermoplastic polyurethane elastomer

Electrostatic Action Induced Interfacial Accumulation of Layered Double Hydroxides Towards Highly Efficient Flame Retardance and Mechanical Enhancement of Thermoplastic Polyurethane/ammonium Polyphosphate

Effect of a bio-based copolymer containing lysine, dopamine and triazine on flame retardancy and mechanical properties of thermoplastic polyurethane/ammonium polyphosphate

Preparation of Ni-Fe layered double hydroxides and its application in thermoplastic polyurethane with flame retardancy and smoke suppression

Core-shell flame retardant/APP-PEI@MXene@ZIF-67: a nanomaterials self-assembly strategy towards reducing fire hazard of thermoplastic polyurethane

Core-shell flame retardants based on Chitosan@MMT coated ammonia polyphosphate for enhancing flame retardancy of polyurethane

Biomass tannic acid intermediated surface functionalization of ammonium polyphosphate for enhancing fire safety and smoke suppression of thermoplastic polyurethane

Surface modification on ammonium polyphosphate and its enhanced flame retardancy in thermoplastic polyurethane

Design of core-multi shell flame retardant towards fire safe thermoplastic polyurethane composites with low toxic fumes generation

Ammonium Polyphosphate/montmorillonite Nanocomposite with a Completely Exfoliated Structure and Charring–foaming Agent Flame Retardant Thermoplastic Polyurethane

Effect carbon black microencapsulated ammonium polyphosphate on the flame retardancy and mechanical properties of polyurethane composites

Preparation of Ammonium Polyphosphate Coated with Aluminium Hydroxide and Its Application in Polypropylene As Flame Retardant

Synergistic Flame Retardant Effect of Ammonium Polyphosphate and Aluminum Hydroxide on Polyurethane

Copper metal‐organic framework toward flame‐retardant enhancement of thermoplastic polyurethane elastomer composites based on ammonium polyphosphate

Fire behavior and mechanical properties of phosphorus-containing silica gel coated ammonium polyphosphate as fire retardants in thermoplastic polyurethane (TPU)