Preparation and Characterization of High Performance Coal Tar Pitch-Based Carbon Fiber
Dakui Zhang,Chunfeng Mu,Ying He,Wei Lai,Haifeng Liu,Qingpei Liu,Jun Yao,Xinyu Zhang,Xiaonan Wang,Zhanqiang Xue,Yi Nie,Kedong Song
DOI: https://doi.org/10.1080/1536383x.2023.2264417
IF: 2.06
2024-01-01
Fullerenes Nanotubes and Carbon Nanostructures
Abstract:High performance carbon fiber based on coal tar pitch is a new type of functional material with unique properties, such as light weight, high strength, high modulus, high thermal conductivity, high electrical conductivity and low thermal expansion coefficient. It is a new type of functional material for both military and civilian use. In order to study the preparation of high performance carbon fiber based on coal tar pitch, this article obtained high performance carbon fiber based on coal tar pitch through raw material pretreatment, spinnable asphalt modulation, asphalt melt spinning, non-melting, carbonization, graphitization and other processes, and characterized the performance of spinnable mesocase asphalt and carbon fiber. The results show that high-performance spinnable mesophase pitch can be prepared by three steps raw material refining, hydrogenation modification and thermal polymerization. The mesophase content is 95%, the softening point is 280 degrees C, and the 3000 m filament can be spun under melt spinning conditions of 375 degrees C and 0.01 MPa. After graphitization, the coal pitch-based carbon fiber has excellent mechanical properties, small structural defects and a diameter of 12 mu m. The tensile strength is 3089 MPa, the elastic modulus is 689 GPa, and the thermal conductivity is 902 w/(m center dot K).