Abstract:A series of laboratory experiments were conducted to investigate the effect of freeze–thaw (FT) cycles on mechanical properties and chloride permeability of concrete with the strength class of C30 in this paper. The mechanical property tests were performed on the specimens subjected to 0, 5, 15, 30, 50, 75 and 100 standard FT cycles to determine the compressive strength, normalized dynamic elastic modulus (NDEM) and mass loss. Also, the chloride natural diffusion tests of concrete specimens, after 0, 5, 15, 30 and 50 FT cycles, were conducted in a self-design tidal cycling simulation device to investigate the chloride ingress into concrete in marine environment of tidal zone. Based on the Fick's second law, a time-dependent model was developed to predict the chloride profiles of frost-damaged concrete. Additional FT cycling tests at different minimum temperatures of freezing process (−4 and −11 °C) and the chloride natural diffusion tests were conducted to study the effect of minimum temperature on the chloride diffusion in concrete. The experimental results revealed the significant influence of FT action on the mass loss, compressive strength and NDEM. After 50 FT cycles, the mean of NDEM dropped to 60%, indicating that the specimen was destroyed by FT action. With the decrease of minimum freezing temperature, the loss of NDEM increased apparently, performing a good linear relation. A substantial effect of FT damage on the chloride profiles was observed: compared to the counterparts of the control groups without being exposed to FT attack, chloride concentration was larger for the frost-damaged concrete, and this difference increased with the extension of exposure duration. A linear relation between the apparent chloride diffusion coefficient and the loss of NDEM was also obtained regardless of the exposure time. Moreover, it was found that the proposed model was applicable for the prediction of chloride profiles in concrete subjected to FT cycles at different minimum freezing temperatures. In other words, the proposed model can be used to describe the chloride ingress into frost-damaged concrete, regardless of the cause of the damage (due to the number of FT cycles or the minimum freezing temperature).

Effect of chloride salt, freeze–thaw cycling and externally applied load on the performance of the concrete

Deterioration characteristics of the bond between reinforcement and concrete subjected to freezing-thawing cycles and steel corrosion

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Macroscopic and Mesoscopic Deterioration Behaviors of Concrete under the Coupling Effect of Chlorine Salt Erosion and Freezing–Thawing Cycle

Concrete Durability after Load Damage and Salt Freeze-Thaw Cycles

Influence of Flexural Loading on Chloride Ingress in Concrete Subjected to Cyclic Drying-Wetting Condition

Experimental Study and Mechanism Analysis on Frost Resistance of Normal Performance Concrete under Different Environments

Durability Of Concrete Under Coupling Effects Of Cyclic Loads And Chloride Environment

Theoretical and Experimental Investigation of Loading Effects on Chloride Diffusion in Saturated Concrete

Chloride Penetration into Concrete Damaged by Uniaxial Tensile Fatigue Loading

Experimental studies on the chloride ion permeability of concrete considering the effect of freeze–thaw damage

Experimental Evaluation of the Concrete Damage and Pore Characteristics under Salt-Freezing Cycles

Chloride penetration in concrete exposed to cyclic drying-wetting and carbonation

Influence of the Coupling Action of Flexural Load and Freezing–Thawing on the Chloride Diffusion of Marine High-Performance Concrete

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Chloride Transport Behavior in Bending-Shear Section of Reinforced Concrete Beam under Combined Effect of Load and Environment

Fracture Behavior of Concrete under Chlorine Salt Attack Exposed to Freeze–Thaw Cycles Environment

Effect of load on bonding properties and salt freeze-thaw resistance of bridge expansion joint concrete

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack