Fracture Behavior of Concrete under Chlorine Salt Attack Exposed to Freeze–Thaw Cycles Environment

Wenhao Li,Shaowei Hu
DOI: https://doi.org/10.3390/ma16186205
IF: 3.4
2023-09-15
Materials
Abstract:Fracture behavior is one of the key properties to study concrete cracking under sodium chloride attack exposed to the freeze–thaw cycles environment, which is frequently neglected. In this paper, 24 single edge notch beam specimens and 24 cubes were poured. The corresponding freeze–thaw cycles test in sodium chloride solution, standard cube compressive strength of concrete test, and three-point-bending tests were carried out. The research revealed that the fracture toughness, fracture energy, relative dynamic modulus of elasticity, and standard cube compressive strength were decreased by increasing freeze–thaw cycles under sodium chloride attack, and the damage degree of concrete caused by sodium chloride solution was deeper than that of pure water. In particular, there existed good linear correlation between the fracture behavior and imposed freeze–thaw damage for various solution. Accordingly, a more reliable damage model using fracture control parameters as damage factors was proposed.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem that this paper attempts to solve is the influence of sodium chloride salt solution on the fracture behavior of concrete in the freeze - thaw cycle environment. Specifically, the research aims to explore the changes in fracture toughness, fracture energy, relative dynamic elastic modulus and standard cube compressive strength of concrete specimens undergoing freeze - thaw cycles in sodium chloride salt solution, and compare them with specimens in pure water environment. The study found that as the number of freeze - thaw cycles increases, the damage degree of concrete in sodium chloride salt solution is deeper than that in pure water. In addition, the research also proposed a more reliable damage model, using fracture control parameters as damage factors to evaluate the damage degree of concrete in sodium chloride salt solution under freeze - thaw cycles. This model is of great significance for understanding the durability of concrete under harsh environmental conditions.