Abstract:Scanning x-ray microbeam topography and fluorescence experiments were conducted in situ to study the electromigration behavior of a 0.5 μm thick, 10 μm wide, and 200 μm long Al(0.25 at. % Cu) conductor line with 1.5 μm-thick SiO2 passivation on a single crystal Si substrate. The strain sensitivity of x-ray topography measurement allowed detailed examination of the electromigration-induced stress distribution and evolution in the conductor line in response to the depletion of Cu solute early in the electromigration process. Upon electromigration at 0.4 MA/cm2 and 303 °C, a short-range stress gradient was quickly induced by Al migration in the Cu-depleted cathode region to counteract further Al flow. The stress gradient was fully developed during the 5.3 h incubation time, extending over the critical Blech length of about 66 μm from the cathode end. Plastic deformation then occurred at the downstream end of the Cu-depleted region. The preferential electromigration of Cu did not cause detectable stress change outside the Cu-depleted region, except for the significant stress development from the Al2Cu precipitation at the anode end which appeared to initiate the fracture in the passivation. Preliminary finite difference modeling was undertaken to simulate the experimental observations, from which important parameters dictating electromigration in Al(Cu) line were extracted: an apparent effective valence of −5.6 and −1.9 for Cu and Al in Al(Cu), respectively, and a critical Cu concentration of 0.16 at. % above which Al grain boundary diffusion is effectively blocked.

First principles calculation of the effects of solute atom on electromigration resistance of Al interconnects

Effects Of Cu On The Electromigration Behavior Of Al Interconnect By Using First-Principles Method

Effects of Sc on the Vacancy and Solute Behaviours in Aluminium

Comparison of the Time-Dependent Physical Processes in the Electromigration of Deep Submicron Copper and Aluminum Interconnects

First-principles Calculations of the Effects of Cu and Ag Additions on the Electromigration of Sn-based Solder

Understanding the Impact of Surface Engineering, Structure, and Design on Electromigration Through Monte Carlo Simulation and In‐Situ SEM Studies

Effect of intermetallic on electromigration and atomic diffusion in Cu/SnAg 3.0Cu 0.5/Cu joints: Experimental and first-principles study

The Effect of Bi Addition on the Electromigration Properties of Sn-3.0Ag-0.5Cu Lead-Free Solder

First-principles study of effects of alloying elements on Cu/γ-Fe interfacial properties

First-principles Study on Solute-Basal Dislocation Interaction in Mg Alloys

Interaction Effect between Electromigration and Microstructure Evolution

An in-situ experimental and simulation study on the electromigration behavior of SAC305 solder joints

Investigation of electromigration in copper interconnection of ULSI

Investigating interfacial segregation of Ω /Al in Al-Cu alloys: A comprehensive study using density functional theory and machine learning

The Study of the Reliability of Complex Components during the Electromigration Process

The inhibition mechanism of liquid metal embrittlement cracks in the Fe–Cu system by Al: atomistic simulations and calculations

Electromigration Effects Upon Interfacial Reactions

First-Principles Study On Stability Of Transition Metal Solutes In Aluminum By Analyzing The Underlying Forces

Characterization of electromigration-induced short-range stress development in Al(0.25 at. % Cu) conductor line

Interdiffusion reliability and resistivity scaling of intermetallic compounds as advanced interconnect materials

The influence of Sc solute partitioning on the microalloying effect and mechanical properties of Al-Cu alloys with minor Sc addition