Controlling the Morphology and Crystal Form of Symmetric Network PVDF Membranes by Bath Temperature

Qian Ye,Li Xing,Lin Zhang,Huanlin Chen

2011-01-01

Abstract:Symmetric network poly(vinylidene fluoride)(PVDF) membranes without dense skin layer were prepared by immersion precipitation in the PVDF/ triethyl phosphate(TEP) system.The effect of coagulation bath temperature on the morphology and crystallization of PVDF membranes was investigated.At higher temperatures,the diffusional mass transfer between the solvent and the non-solvent was enhanced,causing the formation of α-type PVDF crystallites.Thus,PVDF membranes with crystallites that are predominantly β-type could be obtained at lower temperature.The β-type PVDF crystal was polar due to it all-trans arrangement.The interaction of hydrogen bonding or electrostatic force between β-type and bovine serum albumin(BSA) may be stronger than that with α-type.M20-8(TEP coagulation bath 20 ℃,water coagulation bath 8 ℃) can absorb BSA up to 160 μg/cm2.