Abstract:Ferrimagnetic ceramics are an important kind of material used for electronic devices as tunable microwave devices(radar,telecommunication and radio frequency measurement systems),circulators,isolators,phase shifters,tunable filters and nonlinear devices.Re3Fe5O12(Re represents rare earth) is an example of ferrimagnetic ceramics widely applied in passive microwave devices.It belongs to a group of magnetic oxides,characterized by specific magnetic and magnetooptical properties.In this paper,the properties of Lutetium iron garnets are studied carefully.The Lu3Fe5-xMgxO12(x=0,0.025,0.05,0.1,0.15) ceramics were prepared by a solid-state reaction method.Meanwhile,the structure,dielectric properties,magnetic properties,infrared spectra and Raman spectra of the Lu3Fe5-xMgxO12 ceramics were investigated.The X-ray diffraction(XRD) pattern shows that the Lu3Fe5-xMgxO12 samples have the structure of garnet ferrite and no impurity phases are observed.Measurements of magnetization on the samples revealed that Mg doping influenced the magnetic properties.Mg2+ will first substitute the Fe3+ in the octahedron sites than that in the tetrahedron sites leading to enhancement of magnetization with low concentration of Mg2+.However,the magnetization value decreases with larger quantity of Mg dopingas the result of Mg2+ ions entering into the two magnetic sublattices(octahedron and tetrahedron sites) at the same time.Investigations on the IR and Raman spectra reveal the mechanism of the influence on the magnetic properties of the Lu3Fe5O12 ceramics by the Mg doping.

A modification of Lu3Fe5O12 ceramics