Structural and magnetic properties of multiferroic hexagonal Lu0.5(Sc1-In )0.5FeO3 ceramics
Kai Yang,Yuan Yuan,Changcai Chen,Guang Yu,Xiaohua Luo,Shengcan Ma,Sajjad Ur Rehman,Zhenchen Zhong
DOI: https://doi.org/10.1016/j.jallcom.2020.157137
IF: 6.2
2021-02-01
Journal of Alloys and Compounds
Abstract:<p>In this work, we have investigated the structural and magnetic properties of hexagonal Lu<sub>0.5</sub>(Sc<sub>1-<em>x</em></sub>In<sub><em>x</em></sub>)<sub>0.5</sub>FeO<sub>3</sub> ceramics synthesized by solid state reaction. All samples were identified to crystalize in the hexagonal structure with polar space group (). The lattice parameters, both <em>a</em> and <em>c</em>, increase with In-substitution, owing to larger ionic radius of In<sup>3+</sup> in comparison with that of Sc. Meanwhile, the <em>c</em>/<em>a</em> ratio increases from 1.9952 for <em>x</em> = 0 to 2.0308 for <em>x</em> = 1.0. All samples undergo an antiferromagnetic transition, accompanied by a dielectric anomaly, which is the fingerprint of magnetoelectric coupling in hexagonal LuFeO<sub>3</sub> systems. The Néel temperature (<em>T</em><sub>N</sub>) shifts towards lower temperature with the increase of In-substitution, demonstrating the weakening magnetic interaction stemming from smaller structural distortion due to smaller tilting angle of FeO<sub>5</sub> bipyramids. It is fascinating that the increase of <em>c</em>/<em>a</em> ratio brings about a decrease of <em>T</em><sub>N</sub> after the In-substitution for Sc. Another magnetic anomaly was observed above the <em>T</em><sub>N</sub> (around 265 K) in Lu<sub>0.5</sub>Sc<sub>0.5</sub>FeO<sub>3</sub>. The temperature of magnetic anomaly increases towards higher temperature with the increase of In-substitution and rises above room temperature in Lu<sub>0.5</sub>In<sub>0.5</sub>FeO<sub>3</sub>. It can be suggested that the magnetic order is more complex than that obtained in previous works, and the room-temperature multiferroics is attainable for application in hexagonal RFeO<sub>3</sub> systems.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering