Desorption–recombination and Microstructure Change of a Disproportionated Nanostructured NdFeB Alloy

Lianxi Hu,Yuping Li,Yuan,Gang Shi

DOI: https://doi.org/10.1557/jmr.2008.0046

2008-01-01

Abstract:The desorption–recombination behavior of a mechanically disproportionated, nanostructured Nd 12 Fe 82 B 6 alloy was investigated by differential scanning calorimetry and thermogravimetric analysis. The microstructure change due to desorption–recombination treatments at various temperatures was characterized by x-ray diffraction, Mössbauer study, and transmission electron microscopy observation. The results show that the hydrogen desorption of the as-disproportionated alloy occurs in two stages: (i) the partial dehydriding of the Nd hydride from Nd 2 H 5 to NdH 2 , as well as the desorption of the hydrogen absorbed/adsorbed at sites of crystal defects but not in the form of Nd hydride, at temperatures between 180 and 460 °C; and (ii) the complete dehydriding of the Nd hydride from NdH 2 to Nd at temperatures between 630 and 780 °C. The recombination of α-Fe with Fe 2 B and Nd to form Nd 2 Fe 14 B occurs following the dehydriding of NdH 2 to Nd, and it acts as the controlling step for the whole desorption–recombination process. The kinetics of both the desorption–recombination reaction and the growth of the newly formed Nd 2 Fe 14 B grains accelerate with increasing temperature. For a fixed annealing time of 30 min, the optimal processing temperature seems to be 760 °C, which gives rise to a fully recombined Nd 2 Fe 14 B–α-Fe nanocomposite microstructure with Nd 2 Fe 14 B and α-Fe phases of 25–30 nm in average size.